牌号 MT 316L
對應标準 ASTM A554-2016
焊接不鏽鋼機械管
Welded Stainless Steel Mechanical Tubing
歸類 奧氏體不鏽鋼
MT 316L 化學元素成分含量(%)
成分 C ① Si Mn P S Cr Ni Mo
最小值 - - - - - 16 10 2
最大值 0.035 1 2 0.045 0.03 18 15 3
① For small diameter or thin walls, or both, where many drawing passes are required, a carbon content of 0.040 % max is necessary in grades MT-316L. Small outside diameter tubes are defined as those less than 0.500 in. (12.7 mm) in outside diameter and light wall tubes as those less than 0.049 in. (1.24 mm) in average wall thickness.
碳當量計算
MT 316L 機械性能
熱處理或狀态
抗拉強度
σb
Mpa 		屈服點
σs
Mpa 		斷後伸長率或延伸率
δ
% 		硬度
HBW
退火 ≥483 ≥172 ≥35 ≤192
接近匹配牌号 普通結構用奧氏體不鏽鋼管
# 标準 牌号(等級/别名/符号) 化學成分，重量%，最大值，除非另有說明
C Si Mn P S Cr Ni Mo
熱處理
1 ASTM A269/A269M-2014 A269 TP316L, S31603
0.035120.0450.0316-1810-152-3
 HT
2 ASTM A511/A511M-2020 MT 316L
0.035120.040.0316-1810-152-3
 A
3 ASTM A554-2016 MT 316L
0.035120.0450.0316-1810-152-3
 A
4 ASTM A632-2019(2025) TP 316L, S31603
0.03120.0450.0316-1810-142-3
 HT
5 ASTM A778/A778M-2024 A778 TP 316L, S31603
0.03120.0450.0316-1810-142-3
 AM
6 EN 10296-2-2005 X2CrNiMo17-12-2, 1.4404
0.03120.0450.01516.5-18.510-132-2.5
 AW or SA
7 EN 10296-2-2005 X2CrNiMo17-12-3, 1.4432
0.03120.0450.01516.5-18.510.5-132.5-3
 AW or SA
8 EN 10296-2-2005 X2CrNiMo18-14-3, 1.4435
0.03120.0450.01517-1912.5-152.5-3
 AW or SA
9 EN 10297(2)-2005 X2CrNiMo17-12-2, 1.4404
0.03120.0450.01516.5-18.510-14.52-2.5
 SA
10 EN 10297(2)-2005 X2CrNiMo18-14-3, 1.4435
0.03120.0450.01517-1912.5-152.5-3
 SA
11 GB /T 12770-2012 022Cr17Ni12Mo2, S31603, 00Cr17Ni14Mo2
0.030.7520.040.0316-1810-142-3
 ST;W
12 GB /T 14975-2012 022Cr17Ni12Mo2, S31603, 00Cr17Ni14Mo2
0.03120.040.0316-1810-142-3
 BA
MT316L 對應不同标準
1 ASTM A511/A511M-2020 無縫不鏽鋼機械管和空心棒
MT 316L
2 ASTM A554-2016 焊接不鏽鋼機械管
MT 316L
注：數據僅供參考！如有疑問，請填寫"我要糾錯"！