C50 - ISO 683-18-2014

牌号	C50
對應标準	ISO 683-18-2014 熱處理鋼、合金鋼和易切削鋼 -- 第18部分：光面鋼制品 Bright steel products
歸類	碳鋼

C50 化學元素成分含量(%)

成分	C	Si ^①	Mn	P	S	Cr	Ni	Cu	Mo	更多
最小值	0.47	0.1	0.6	-	-	-	-	-	-	Cr+Mo+Ni≤0.63
最大值	0.55	0.4	0.9	0.045	0.045	0.4	0.4	0.3	0.1	Cr+Mo+Ni≤0.63

① Steels may be supplied with a lower silicon content. In this case, alternative means of deoxidation shall be used.
② Steels with improved machinability either by higher sulfur levels up to about 0,10 % S (including controlled sulphide morphology) or lead additions may be available on request. In the first case, the upper limit of the Mn-content may be increased by 0,15 %.

碳當量計算

C50 機械性能

厚度 t mm	熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	硬度 HBW
5≤t≤10	Cold drawn (+C)	770~1100	≥590	≥5
10＜t≤16	Cold drawn (+C)	730~1080	≥520	≥6
16＜t≤40	Cold drawn (+C)	690~1050	≥440	≥7
40＜t≤63	Cold drawn (+C)	650~1030	≥390	≥8
16＜t≤100	As-rolled + peeled (+SH)	610~910			179~269

注：Steels C50 in delivery condition +C may be soft annealed before cold drawing.

1 近似對照表碳素結構鋼和工程用鋼

中國	日本	國際标準組織
GB	JIS	ISO
50	S50C	C50

2 近似對照表優質碳素結構鋼

中國	日本	美國	國際标準組織	德國	法國	歐标		俄羅斯	瑞典	英國
GB	JIS	ASTM	ISO	DIN EN/DIN	NF EN/NF	EN	數字牌号	GOST	SS	BS EN/BS
50	S50C	1049 1050	C50 C50E4	C50 Ck50	XC48H1	C50	1.0540	50	1674	070M50 080M50

3 近似對照表優質碳素結構鋼

中國	日本	美國	國際标準組織	法國	俄羅斯	英國
GB	JIS	ASTM/AISI	ISO	NF EN/NF	GOST	BS EN/BS
GB/T 699-1999 50	S50C	1049 1050	ISO 630-1:1987 C50 C50E4 C50M2	C50 XC48	50	060A52

C50 對應不同标準

1	ISO 683-18-1996 熱處理鋼、合金鋼和易切削鋼
	C50
2	DIN 17200-1987 調質鋼材的供貨技術條件
	C50 1.0540
3	EN 10250-2-2000 一般工程用自由鍛鋼鍛件.第2部分:非合金鋼和特種鋼
	C50 1.0540
4	ISO 683-1-2016 淬火和回火用非合金鋼
	C50
5	DIN EN ISO 683-1-2018 熱處理鋼、合金鋼和易切削鋼 -- 第1部分：調質非合金鋼
	C50
6	ISO 683-18-2014 熱處理鋼、合金鋼和易切削鋼 -- 第18部分：光面鋼制品
	C50
7	NF A 37-502-1984 結構鋼冷軋鋼帶
	C50

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！