C50E - ISO 683-18-2014 - 材數庫

牌号	C50E
對應标準	ISO 683-18-2014 熱處理鋼、合金鋼和易切削鋼 -- 第18部分：光面鋼制品 Bright steel products
歸類	碳鋼

C50E 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	更多
最小值	0.47	0.1	0.6	-	-	-	-	-	-	Cr+Mo+Ni≤0.63
最大值	0.55	0.4	0.9	0.025	0.035	0.4	0.4	0.3	0.1	Cr+Mo+Ni≤0.63

碳當量計算

C50E 機械性能

厚度 t mm	熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	硬度 HBW
5≤t≤10	Cold drawn (+C)	770~1100	≥590	≥5
10＜t≤16	Cold drawn (+C)	730~1080	≥520	≥6
16＜t≤40	Cold drawn (+C)	690~1050	≥440	≥7
40＜t≤63	Cold drawn (+C)	650~1030	≥390	≥8
16＜t≤100	As-rolled + peeled (+SH)	610~910			179~269
16＜t≤40	Quenched and tempered and peeled (+QT+SH)	700~850	≥460	≥15
40＜t≤100	Quenched and tempered and peeled (+QT+SH)	650~800	≥400	≥16
5≤t≤10	Quenched and tempered + cold drawn (+QT +C)	870~1070	≥610	≥7
10＜t≤16	Quenched and tempered + cold drawn (+QT +C)	830~1030	≥580	≥7
16＜t≤40	Quenched and tempered + cold drawn (+QT +C)	790~990	≥555	≥8
40＜t≤63	Quenched and tempered + cold drawn (+QT +C)	730~930	≥510	≥9
63＜t≤100	Quenched and tempered + cold drawn (+QT +C)	680~880	≥475	≥9

近似對照表淬火和回火用非合金鋼

中國	日本	國際标準組織	歐标
GB	JIS	ISO	EN	數字牌号
50	S50C	C50E	C50E	1.1206

C50E 對應不同标準

1	EN 10083-2-2006 淬火和回火鋼.第2部分:非合金鋼交貨技術條件
	C50E 1.1206
2	ISO 683-1-2016 淬火和回火用非合金鋼
	C50E
3	DIN EN ISO 683-1-2018 熱處理鋼、合金鋼和易切削鋼 -- 第1部分：調質非合金鋼
	C50E
4	ISO 683-18-2014 熱處理鋼、合金鋼和易切削鋼 -- 第18部分：光面鋼制品
	C50E
5	EN 10132-2021 熱處理冷軋窄帶鋼-交貨技術條件
	C50E 1.1206
6	NF EN 10083-2-2006 調質非合金結構鋼
	C50E 1.1206

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！