F436 Type 1 - ASTM F436/436M-2019-材數庫

牌号	F436 Type 1
對應标準	ASTM F436/436M-2019 淬火鋼墊圈的标準規範 Hardened Steel Washers Inch and Metric Dimensions
歸類	碳鋼

F436 Type 1 化學元素成分含量(%)

	成分	P	S
Heat analysis	最小值	-	-
Heat analysis	最大值	0.04	0.05

	成分	P	S
Product analysis	最小值	-	-
Product analysis	最大值	0.05	0.06

碳當量計算

F436 Type 1 機械性能

	硬度 HBW
Through hardened washers	HRC 38~45
zinc-coated by the hot-dip	HRC 26~45

① Through hardened washers shall have a hardness of 38 to 45 HRC, except when zinc-coated by the hot-dip process, in which case they shall have a hardness of 26 to 45 HRC.
② Carburized washers shall be carburized to a minimum depth of 0.015 in. (inch series) or 0.38 mm (metric series) and shall have a surface hardness of 69 to 73 HRA or 79 to 83 HR15N, except when zinc-coated by the hot-dip process, in which case they shall have a hardness of 63 to 73 HRA or 73 to 83 HR15N.
③ Carburized and hardened washers shall have a minimum core hardness of 30 HRC or 65 HRA.

F436Type1 對應不同标準

1	ASTM F436/436M-2016 淬火鋼墊圈的标準規範
	F436 Type 1
2	ASTM F436/436M-2019 淬火鋼墊圈的标準規範
	F436 Type 1
3	ASTM F436/436M-2024 淬火鋼墊圈的标準規範
	F436 Type 1

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！

版權說明：
⑴ 本網站的所有内容（包括但不限于文字、圖片、音頻、視頻等）均受到版權保護，版權歸本網站所有；
⑵ 未經授權，禁止以任何形式轉載、複制、傳播或用于其他商業用途；
⑶ 如需使用本網站内容，請提前獲得授權。