S275M 1.8818 - EN 10025-4-2019

牌号	S275M
歐标鋼号	1.8818
對應标準	EN 10025-4-2019 熱機械軋制可焊接細晶粒結構鋼 Technical Delivery Conditions for Thermomechanical Rolled Weldable Fine Grain Structural Steels
歸類	合金鋼

S275M 化學元素成分含量(%)

成分	C ^④	Si	Mn	P ^①	S ^①②	Cr	Ni	Cu	Mo	N	Ti	V	Nb	Al ^③
最小值	-	-	-	-	-	-	-	-	-	-	-	-	-	0.02
最大值	0.13	0.5	1.5	0.025	0.025	0.3	0.3	0.55	0.1	0.015	0.05	0.08	0.05	-

① For long products the P and S content can be 0.005% higher.
② For some applications, e.g. for railways, a maximum S content of 0,010 % may be agreed upon at the time of the order.
③ If sufficient other N-binding elements are present the minimum total Al content does not apply.
④ For long products a maximum C content of 0,15 % for grade S275.

碳當量計算

S275M 機械性能

厚度 t mm	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %
t≤16	370~530	≥275	≥24
16＜t≤40	370~530	≥265	≥24
40＜t≤63	360~520	≥255	≥24
63＜t≤80	350~510	≥245	≥24
80＜t≤100	350~510	≥245	≥24
100＜t≤150	350~510	≥240	≥24

近似對照表結構、壓力容器和工程鋼

德國	歐标
DIN EN/DIN	EN	數字牌号
StE285TM	S275M FeE275KGTM①	1.8818

S275M 對應不同标準

1	EN 10025-4-2004 結構鋼熱軋產品第4部分熱機械軋制可焊接細晶粒結構鋼
	S275M 1.8818
2	EN 10025-4-2019 熱機械軋制可焊接細晶粒結構鋼
	S275M 1.8818

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！