基本信息
牌号 ENiCrFeCo
W83002
對應标準 AWS A5.13/A5.13M-2010
堆焊焊條規範 保護金屬電弧焊
Specification for Surfacing Electrodes for Shielded Metal Arc Welding
标簽 鎳基堆焊焊條
說明 Characteristics. Weld metal deposited by these electrodes contain a fairly large volume fraction of hypereutectic chromium carbides distributed throughout the microstructure. The alloy offers many of the same high-performance characteristics of deposits made using ECoCr-C or ENiCr-C electrodes in terms of abrasive wear resistance. The reduced nickel or cobalt content, or both, lowers corrosion properties and galling resistance. The high volume fraction of carbides makes this alloy sensitive to cracking during cooling.
Applications. Welds made using ENiCrFeCo electrodes are preferred where high abrasion (low impact) is a major factor. Typical applications are feed screws, slurry pumps, and mixer components.
類别 合金鋼
化學成分
ENiCrFeCo 化學元素成分含量(%)
成分 Fe C Si Mn P S Cr Ni Mo W Co 其他合計
最小值 20 2.2 0.6 - - - 20 10 7 2 10 -
最大值 25 3 1.5 1 0.03 0.03 30 33 10 4 15 1
其他單個或其他合計化學成分包括表中未指定值的化學成分。隻有在假定存在或在常規分析中，且有迹象表明其成分将超過規定值的情況下，才應進行分析。
注：數據僅供參考！如有疑問，請填寫"我要糾錯"！
版權說明：
⑴ 本網站的所有内容（包括但不限于文字、圖片、音頻、視頻等）均受到版權保護，版權歸本網站所有；
⑵ 未經授權，禁止以任何形式轉載、複制、傳播或用于其他商業用途；
⑶ 如需使用本網站内容，請提前獲得授權。

材料與專利鋼号免責聲明：
⑴ 本平台所收錄的部分材料牌号為企業專利鋼号或專有命名牌号，非 GB、ISO、DIN、ASTM、JIS 等通用标準鋼号；
⑵ 相關化學成分、力學性能及适用範圍以專利文件、權利人公開資料或供方技術文件為準；
⑶ 平台所展示信息僅用于材料檢索、工程參考及技術對比，不構成等同、替代或采購依據。
摘要 / Summary
ENiCrFeCo 材料牌号數據，對應标準：AWS A5.13/A5.13M-2010，主要化學成分：Fe 20–25%，C 2.2–3%，Si 0.6–1.5%，Mn ≤1%，P ≤0.03%，S ≤0.03%，Cr 20–30%，Ni 10–33%，Characteristics. Weld metal deposited by these electrodes contain a fairly large volume fraction of hypereutectic chromium carbides distributed throughout the microstructure。