B2 - BS 3100-1991 - 材數庫

牌号	B2
對應标準	BS 3100-1991 一般工程用鑄鋼件 Specification for Steel Castings for General Engineering Purposes
歸類	鑄鋼
标簽	高溫用合金鋼鑄鋼

B2 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni ^①	Cu ^①	Mo
最小值	-	-	0.5	-	-	1	-	-	0.45
最大值	0.2	0.6	0.8	0.04	0.04	1.5	0.4	0.3	0.65

①殘餘元素。

碳當量計算

B2 機械性能

熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	沖擊吸收能量 KV2 J
N+T或OQ+T或WQ+T(T 700°C max)	≥480	≥280	≥17	≥30

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

B2 對應不同标準

1	JIS G 7401-2000 冷鍛及冷軋擠壓用鋼
	(B2) CE15E4
2	ISO 4954-1993 冷镦和冷擠壓用鋼
	(B2) CE15E4
3	ASTM B103/B103M-2019 磷青銅闆、薄闆、帶材和軋制棒材
	(B2) B103 C54400
4	ASTM A485-2014 高淬透性耐磨軸承鋼的技術規範
	B2 A485 100CrMnSi 4-4
5	ASTM A485-2017 高淬透性耐磨軸承鋼的技術規範
	B2 100CrMnSi 4-4
6	BS 3100-1991 一般工程用鑄鋼件
	B2