410C21 - BS 3100-1991

牌号	410C21
對應标準	BS 3100-1991 一般工程用鑄鋼件 Specification for Steel Castings for General Engineering Purposes
歸類	鑄鋼
性能	耐腐蝕
标簽	不鏽鋼鑄鋼

410C21 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Cu ^①
最小值	-	-	-	-	-	11.5	-	-
最大值	0.15	1	1	0.04	0.04	13.5	1	0.3

①殘餘元素

碳當量計算

410C21 機械性能

熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %
AH+T或OQ+T(T at 750°C max)	≥540	≥370	≥15

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

1 近似對照表耐蝕鑄鋼（不鏽鋼鑄件）

中國

中國台灣

日本

韓國

美國

國際标準組織

德國

法國

俄羅斯

瑞典

英國

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

SS₁₄

BS EN/BS

ZG15Cr12

C54100

SCS 1

SCS 1X

SSC 1

CA15

J91150

GX12Cr12

1.4011

Z12C13M

15Х13Л

2302

410C21

2 近似對照表耐蝕鑄鋼（不鏽鋼鑄件）

中國	日本	美國	德國		法國	俄羅斯	英國
GB	JIS	ASTM	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG1Cr13	SUS1	CA15	G-X8Cr14 X15Cr13	1.4008 1.4024	Z12C13M	15Х13Л	410C21

3 近似對照表耐熱鑄鋼和耐熱合金鑄件

中國	日本	美國		德國		法國	俄羅斯	英國
GB	JIS	ASTM	UNS	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG1Cr13	SCS1	CA15	J91150	G-X7Cr13 G-X10Cr13	1.4001 1.4006	Z12C13M	15Х13Л	410C21