牌号 304C12
對應标準 BS 3100-1991
一般工程用鑄鋼件
Specification for Steel castings for general engineering purposes
歸類 鑄鋼
性能 耐腐蝕
标簽 奧氏體不鏽鑄鋼 有磁性
304C12 化學元素成分含量(%)
成分 C Si Mn P S Cr Ni
最小值 - - - - - 17 8
最大值 0.03 1.5 2 0.04 0.04 21 12
碳當量計算
304C12 機械性能
熱處理或狀态
抗拉強度
σb
Mpa 		屈服點
σs
Mpa 		斷後伸長率或延伸率
δ
%
ST(1000°C~1100°C) ≥430 1% proof stress Rp1.0 min ≥240
≥215		 ≥26
A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.
1 近似對照表 耐蝕鑄鋼（不鏽鋼鑄件）
中國 中國台灣 日本 韓國 美國 國際标準組織 德國 法國 俄羅斯 英國
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG03Cr18Ni10 C53043 SCS 19A SCS 19A SSC 19A CF3 J92500 GX2CrNiMo18-10 GX2CrNiMo19-11 1.4309 Z2CN18.10M 03Х18Н9Л 304C12
2 近似對照表 耐蝕鑄鋼（不鏽鋼鑄件）
中國 中國台灣 日本 韓國 美國 國際标準組織 德國 法國 俄羅斯 英國
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG03Cr18Ni10 C53043 SCS 19A SCS 36 SSC 19A CF3 J92500 GX2CrNi18-10 GX2CrNi19-11 1.4309 Z2CN18.10M 03Х18Н9Л 304C12
3 近似對照表 耐蝕鑄鋼（不鏽鋼鑄件）
中國 日本 美國 德國 法國 俄羅斯 英國
GB JIS ASTM DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG00Cr18Ni10 SUS19 CF3 G-X2CrNi18 9 1.4306 Z2CN18.10M Х18Н8Л(舊号) 304C12
4 近似對照表 耐熱鑄鋼和耐熱合金鑄件
中國 日本 美國 德國 法國 俄羅斯 英國
GB JIS ASTM UNS DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG00Cr18Ni10 SCS19 CF3 J92500 G-X2CrNi18 9 1.4036 Z2CN18.10M 03Х18Н11 304C12
注：數據僅供參考！如有疑問，請填寫"我要糾錯"！