316C16 - BS 3100-1991

牌号	316C16
對應标準	BS 3100-1991 一般工程用鑄鋼件 Specification for Steel castings for general engineering purposes
歸類	鑄鋼
性能	耐腐蝕
标簽	奧氏體不鏽鑄鋼有磁性

316C16 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Mo
最小值	-	-	-	-	-	17	9	2
最大值	0.08	1.5	2	0.04	0.04	21	-	3

碳當量計算

316C16 機械性能

熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %
ST(1050°C~1150°C)	≥480	1% proof stress Rp1.0 min ≥240	≥26

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

近似對照表耐熱鑄鋼和耐熱合金鑄件

日本	美國		德國		法國	英國
JIS	ASTM	UNS	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
SCS14	CN-7M	J95150	G-X12Cr14	1.4008	Z12CN13-M	316C16

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！