330C12 - BS 3100-1991

牌号	330C12
對應标準	BS 3100-1991 一般工程用鑄鋼件 Specification for Steel castings for general engineering purposes
歸類	鑄鋼
性能	耐腐蝕
标簽	耐熱不鏽鑄鋼

330C12 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Mo
最小值	-	-	-	-	-	13	30	-
最大值	0.75	3	2	0.05	0.05	20	40	1.5

碳當量計算

330C12 機械性能

熱處理或狀态	抗拉強度 σ_b	屈服點 σ_s	斷後伸長率或延伸率 δ %	硬度 HBW	沖擊吸收能量 KV2 J
N或N+T或QQ+T或WQ+T	540~690	≥320	≥16	152~207	≥30

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.