310C40 - BS 3100-1991

牌号	310C40
對應标準	BS 3100-1991 一般工程用鑄鋼件 Specification for Steel castings for general engineering purposes
歸類	鑄鋼
性能	耐腐蝕
标簽	耐熱不鏽鑄鋼有磁性

310C40 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Mo
最小值	0.3	-	-	-	-	24	19	-
最大值	0.5	1.5	2	0.04	0.04	27	22	1.5

碳當量計算

310C40 機械性能

熱處理或狀态	抗拉強度 σ_b Mpa	斷後伸長率或延伸率 δ %
As cast	≥450	≥7

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

1 近似對照表耐熱鑄鋼和耐熱合金鑄件

中國

中國台灣

日本

韓國

美國

國際标準組織

德國

法國

俄羅斯

英國

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

ZG40Cr25Ni20Si2

C53901

SCH 21

HRSC 21

HK30

J94203

GX40NiCrSi25-20

1.4848

Z40CN25.20M

≈15Х23Н18Л

310C40

2 近似對照表耐蝕鑄鋼（不鏽鋼鑄件）

中國	日本	美國	德國		英國
GB	JIS	ASTM	DIN EN/DIN	W-Nr.	BS EN/BS
ZG4Cr25Ni20Si2	SCH22	HK40	G-X40CrNiSi2520	1.4848	310C40

3 近似對照表耐熱鑄鋼和耐熱合金鑄件

中國	日本	美國		德國		英國
GB	JIS	ASTM	UNS	DIN EN/DIN	W-Nr.	BS EN/BS
ZG4Cr25Ni20Si2	SCH22	HK HK-40	J94224 J94204	G-X40CrNiSi25 20	1.4848	310C40 310C45

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！