AMS 6471H - SAE AMS 6471H-2014 - 材數庫

牌号	AMS 6471H
對應标準	SAE AMS 6471H-2014 真空熔煉氮化鋼棒材、鍛件和管材1.6Cr-0.35Mo-1.13Al(0.38~0.43C)(135 Mod) Steel, Nitriding, Bars, Forgings, and Tubing 1.6Cr-0.35Mo-1.13Al(0.38~0.43C)(135 Mod) Consumable Electrode Vacuum Melted
歸類	合金鋼
說明	Application These products have been used typically for nitrided parts requiring high surface hardness, resistance to heat, and less distortion than parts fabricated form steel requiring quenching to case harden and subject to very rigid inspection standards, but usage is not limited to such applications. This steel may be case hardened in dissociated ammonia gas to provide a minium case hardess of 900 HV.

AMS 6471H 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	Al
最小值	0.38	0.2	0.5	-	-	1.4	-	-	0.3	0.95
最大值	0.43	0.4	0.8	0.015	0.015	1.8	0.25	0.35	0.4	1.3

碳當量計算

AMS 6471H 機械性能

條件	熱處理或狀态	抗拉強度 σ_b Mpa	硬度 HBW
棒材d≤12.7	冷拔	≤931
棒材d>12.7	熱拔+退火		≤229
棒材d>12.7	熱拔+退火		≤269
管材	冷拔		HRC ≤25
管材	熱拔+退火		HRB ≤99

鍛件的機械性能按協議

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！