X50CrMnNiNbN21-9 1.4882 - EN 10090-1998

牌号	X50CrMnNiNbN21-9
歐标鋼号	1.4882
對應标準	EN 10090-1998 内燃機用氣門鋼和合金 Valve steels and alloys for internal combustion engines
歸類	合金鋼
性能	耐腐蝕
标簽	奧氏體鋼

X50CrMnNiNbN21-9 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	N	W	更多
最小值	0.45	-	8	-	-	20	3.5	0.4	0.8	Nb+Ta:1.8~2.5
最大值	0.55	0.45	10	0.045	0.03	22	5.5	0.6	1.5	Nb+Ta:1.8~2.5

碳當量計算

X50CrMnNiNbN21-9 機械性能

條件	試驗溫度	熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	斷面收縮率 ψ %	硬度 HBW
鋼材	室溫	Controlled cooled	≈1300				≈385
鋼材	室溫	Quenched at 1000°C to 1100°C	≤1300				≤385
鋼材d≤40	室溫	+AT +P	950~1150	≥580	≥12	≥15	HRC≥30*
鋼材	500°C	+AT +P	≥680	≥350
鋼材	550°C		≥650	≥330
鋼材	600°C		≥610	≥310
鋼材	650°C		≥550	≥285
鋼材	700°C		≥480	≥260
鋼材	750°C		≥410	≥240
鋼材	800°C		≥340	≥220

① +QT = quenched and tempered; +AT = solution annealed; +P = precipitation hardened；+A=Soft annealed

*Austenitic grades X55CrMnNiN20-8 to X33CrNiMnN23-8 may show hardness values which cannot be converted into tensile strength
values acording to the standard tables commonly used in laboratories. Therefore, in cases of dispute only the tensile strength value
shall be considered as valid.

近似對照表奧氏體型耐熱鋼

中國	國際标準組織	歐标
GB	ISO	EN	數字牌号
50Cr21Mn9Ni4Nb2WN	X50CrMnNiNbN 21-9	X50CrMnNiNbN 21-9	1.4882

X50CrMnNiNbN21-9 對應不同标準

1	EN 10090-1998 内燃機用氣門鋼和合金
	X50CrMnNiNbN21-9 1.4882
2	NF EN 10090-1998 閥門用鋼和合金
	X50CrMnNiNbN21-9 1.4882

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！