42CrMo5-6 1.7233 - NF EN 10269-1999

牌号	42CrMo5-6
	1.7233
對應标準	NF EN 10269-1999 用于高溫或低溫條件下的緊固件用鋼及鎳合金
歸類	合金鋼
标簽	淬火回火鋼

42CrMo5-6 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Mo
最小值	0.39	-	0.4	-	-	1.2	0.5
最大值	0.45	0.4	0.7	0.035	0.035	1.5	0.7

◎ 未經買方同意，不得随意向鋼中添加表中未列的元素，冶煉精加工除外。采用一切必要措施以防在廢鋼和生產原料中帶入這些元素，因為其會削弱鋼的機械性能，降低鋼的适用性

碳當量計算

42CrMo5-6 機械性能

直徑 d mm	熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	斷面收縮率 ψ %	硬度 HBW	沖擊吸收能量 KV2 J
-*	+S	-	-	-	-	≤255	-
-*	+A	-	-	-	-	≤241	-
d≤100**	+QT	860~1060	≥700	≥16	≥50	-	≥50
100＜d≤150**	+QT	850~1000	≥640	≥16	≥50	-	≥40

◎ +AT=固溶退火；+C=冷作硬化；+N=正火；+NT=正火及回火；+P=沉澱硬化；+QT=淬火及回火；WW=熱作硬化；+AC=球化退火；+A=軟化退火；+S=冷剪處理（treated for cold shearing）

*通常适用于進一步加工交貨條件下的常溫機械性能
**鋼在室溫和20攝氏度交貨條件下的機械性能，符合97/23/EC的基本安全要求

交付條件下在高溫下的最小屈服強度

Material designation		Heat treatment condition	Diameter d mm	Minimum 0.2%-proof strength R_p0.2 in MPa at a temperature (in°C) of:
Name	Number	Heat treatment condition	Diameter d mm	50	100	150	200	250	300	350	400	450	500	550	600	650
42CrMo5-6	1.7233	+QT	d≤100	681	662	639	616	601	585	570	547	516	462	362	223	-
42CrMo5-6	1.7233	+QT	100＜d≤150	625	605	584	563	549	535	521	500	472	422	331	204	-

符合本歐洲标準的產品熱處理指南

Material designation		Heat treatment condition	Normalizing,quenching or solution annealing temperature °C	Type of cooling^①	Tempering or precipitation treatment (and time) °C
Name	Number
42CrMo5-6	1.7233	+QT	840 to 870	o	600 to 700

◎ 根據原件相關規定，如果允許矯直後消除應力，應選擇消除應力的溫度，以獲得規定的性能。
① a=air; o=oil; w=water

蠕變性能

Designation		Temperature	Strength for 1% (plastic) creep strain ①		Creep rupture strength for ②
Name	Number	°C	10000h	100000h	10000h	100000h	200000h
42CrMo5-6	1.7233	450	-	-	495	410	381
		460	-	-	450	345	310
		470	-	-	399	276	242
		480	-	-	342	219	193
		490	-	-	281	177	158
		500	-	-	229	148	131
		510	-	-	190	124	109
		520	-	-	160	102	84
		530	-	-	137	-	-
		540	-	-	118	-	-
		550	-	-	98	-	-

◎ The values given in this table are the mean values of the scatter band so far obtained, which will be checked from time to time as further test results become available and if necessary corrected.
◎ * and () indicate values of extended stress extrapolation or time extrapolation, respectively.
① This is the stress relative to the initial cross- section leadina to a permanent elongation of 1 % after 10000 h and 100000 h.
② This is the stress relative to the initial cross- section leading to fracture after 10000 h, 100000 h and 200000 h.

松弛性能

Material designation		Temperature ℃	for an initial strain ∈_{A total} %	Residual stress in N/mm² after stressing duration for
Name	Number	Temperature ℃	for an initial strain ∈_{A total} %	1000 h	10000 h	30000 h
42CrMo5-6	1.7233	350	0.15	211	205	201
		400		198	179	164
		450		157	118	96
		500		93	30	-

42CrMo5-6 對應不同标準

1	EN 10269-2006 規定高溫和/或低溫性能的緊固件用鋼和鎳合金
	42CrMo5-6 1.7233
2	EN 10269-2013 規定高溫和/或低溫性能的緊固件用鋼和鎳合金
	42CrMo5-6 1.7233
3	NF EN 10269-1999 用于高溫或低溫條件下的緊固件用鋼及鎳合金
	42CrMo5-6 1.7233
4	DIN EN 10269-2014 規定高溫和/或低溫性能的緊固件用鋼和鎳合金
	42CrMo5-6 1.7233

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！