01 鋼鐵產品處理狀态符号
核心作用：标識鋼鐵產品的加工或熱處理狀态，反映產品的工藝特性。
符号規則：符号與前面的名稱用 “+” 分隔。
主要符号及含義：
代号 | 含義（英） | 含義（中） |
+A | soft annealed | 軟化退火 |
+AC | Annealed to achieve spheriodised carbides | 球化退火 |
+AR | as rolled (without any special rolling and/or heat treatment conditions) | 軋制（無任何特殊軋制和/或熱處理條件） |
+AT | solution annealed | 固溶退火 |
+C | cold work hardened | 冷作(拉)硬化 |
+Cnnn | cold work hardened with a minimum tensile strength of nnn MPa | 冷加工硬化，最低抗拉強度為nnn MPa |
+CPnnn | cold work hardened with a minimum 0.2% proof strength of nnn MPa | 冷加工硬化，最低屈服強度為nnn Mpa |
+CR | cold rolled | 冷軋 |
+DC | delivery condition at manufacturer's discretion | 交貨條件由制造商決定 |
+FP | treated to ferritic-pearlite structure and hardness range | 經過處理獲得鐵素體－球光體結構，且達到硬度範圍 |
+HC | hot rolled followed by cold hardening | 熱軋後冷硬化 |
+I | isothermically treated | 恒溫退火 |
+LC | skin passed (temper rolled or cold drawn) | 平整（回火軋制或冷拔） |
+M | thermomechanically formed | 熱機械成形 |
+N | normalised or normalised formed | 正火或正火成形 |
+NT | normalised and tempered | 正火和回火 |
+P | precipitation hardened | 沉澱硬化 |
+Q | quenched | 淬火 |
+QA | air quenched | 空冷淬火 |
+QO | oil quenched | 油淬 |
+QT | quenched and tempered | 淬火和回火，調質 |
+QW | water quenched | 水淬 |
+RA | recrystallisation annealed | 再結晶退火 |
+S | treated for cold shearing | 冷剪處理 |
+SR | stress relieved | 應力消除 |
+T | tempered | 回火 |
+TH | treatment to hardness range | 處理到硬度範圍 |
+U | untreated | 未經處理的 |
+WW | warm worked | 熱作 |
02 鋼鐵產品鍍層及特殊要求符号
核心作用：标識鋼鐵產品的特殊性能要求，這些要求通常屬于鋼鐵本身特性，因實際需要作為產品符号處理。
符号規則：符号與前面的名稱用 “+” 分隔。
主要符号及含義：
代号 | 含義（英） | 含義（中） |
+CH | core hardenability | 芯部可淬性 |
+H | hardenability | 可淬透性 |
0 | through thickness property; minimum reduction of area= 15 % | 厚度方向性能級别；最小斷面收縮率=15% |
0 | through thickness property; minimum reduction of area = 25 % | 厚度方向性能級别；最小斷面收縮率=25% |
0 | through thickness property; minimum reduction of area = 35 % | 厚度方向性能級别；最小斷面收縮率=35% |
+A | hot dip aluminium coating | 熱浸鋁塗層 |
+AS | aluminium silicon alloy coating | 鋁矽合金塗層 |
+AZ | aluminium zinc alloy(> 50 % Al) coating | 鋁鋅合金（>50%鋁）塗層 |
+GE | electrolytic chromium/chromium oxide coating (EGGS) | 電解鉻/氧化鉻塗層(EGGS) |
+CU | copper coating | 鍍銅 |
+IC | inorganic coating | 無機塗料 |
+OC | organic coating | 有機塗層 |
+S | hot dip tin coating | 熱浸鍍錫 |
+SE | electrolytic tin coating | 電解鍍錫 |
+T | hot dip lead tin alloy (terne) coating | 熱浸鉛錫合金鍍層 |
+TE | electrolytic lead tin alloy (terne) coating | 電解鉛錫合金鍍層 |
+Z | hot dip zinc (galvanised) coating | 熱浸鋅（鍍鋅）塗層 |
+ZA | hot dip zinc aluminium(> 50 % Zn) coating | 熱浸鍍鋅鋁（>50%鋅）塗層 |
+ZE | electrolytic zinc coating | 電解鍍鋅 |
+ZF | hot dip zinc iron (galvannealed) coating | 熱浸鍍鋅鐵（電鍍）塗層 |
+ZN | electrolytic zinc nickel alloy coating | 電解鋅鎳合金鍍層 |
03 鋼鐵產品選擇示例
場景示例1 橋梁結構用高強度鋼闆（需厚度方向性能與抗腐蝕塗層）需求分析：橋梁承重結構需承受垂直載荷和環境腐蝕，要求鋼闆具備良好的厚度方向力學性能（避免層狀撕裂）和抗大氣腐蝕能力。
符号選擇 ：
需厚度方向性能，最小斷面收縮率 25%，故添加+Z25；
需抗大氣腐蝕的熱浸鋅塗層，添加+Z；
基礎鋼種：選用結構鋼 S355J2
最終鋼名：S355J2+Z25+Z
該鋼種滿足橋梁對強度、低溫韌性、厚度方向性能的要求，鍍鋅塗層可延長戶外服役壽命。
場景示例2 汽車底盤冷沖壓件（需冷作硬化與磷化前處理）
需求分析：汽車底盤部件需通過冷沖壓成形，要求材料冷作硬化後強度達标，且表面狀态适合後續磷化處理（需冷軋基底）。符号選擇：
冷作硬化後最小抗拉強度 300MPa，添加+C300；且需冷軋基底，添加+CR。
基礎鋼種：選用冷成形用扁平材DC04。
最終鋼名：DC04+CR+C300
冷軋狀态（+CR）保證良好的沖壓成形性，冷作硬化（+C300）提升強度，滿足底盤部件的力學與加工要求。
需求分析：化工管道輸送高溫高壓介質，要求鋼管具備均勻的淬透性（保證整體力學性能一緻）和耐酸堿腐蝕的表面塗層。
符号選擇：
需整體淬透性，添加+H。
采用電解鉻/氧化鉻塗層（耐化學腐蝕），添加+CE。
基礎鋼種：選用13CrMo4-5
最終鋼名：13CrMo4-5+H+CE
淬透性符号（+H）确保管道壁厚方向性能均勻，CE 塗層可抵抗介質腐蝕，适合化工環境使用。
需求分析：電機鐵芯需低鐵損、高磁導率，且需經退火消除應力以穩定磁性能，表面無需塗層（避免影響疊片效率）。
符号選擇
基礎鋼種：選用電工鋼 M400-50A（依據表 11，鐵損 4.00W/kg，無取向）。
需軟化退火消除應力，添加+A。
無需塗層，不添加符号。
基礎鋼種：選用電工鋼 50W400
最終鋼名：50W400+A
退火處理（+A）降低鐵芯損耗，無塗層設計保證疊片時的緊密貼合，提升電機效率。