Type 403 S40300 - ASTM A580/A580M-2018

牌号	Type 403
美國UNS	S40300
對應标準	ASTM A580/A580M-2018 不鏽鋼絲 Stainless Steel Wire
歸類	馬氏體不鏽鋼

Type 403 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr
最小值	-	-	-	-	-	11.5
最大值	0.15	0.5	1	0.04	0.03	13

碳當量計算

Type 403 機械性能

條件	熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	斷面收縮率 ψ %	硬度 HBW
A	冷精軋	≥485	≥275	≥16	≥45
A	退火	≥485	≥275	≥20	≥45
T	冷精軋	≥690	≥550	≥12	≥40
H	冷精軋	≥830	≥620	≥12	≥40
t≤9.5mm	955℃，空冷					HRC ≥35

注1：Condition A —— Annealed as a final heat treatment.
Material in Condition A may be given a final cold drawing for size control or finish, or both, slightly raising tensile strength.
Condition T —— Heat treated to an intermediate temper generally by austenitizing, quenching, and tempering at a relatively low temperature.
Condition H —— Heat treated to a hard temper generally by austenitizing, quenching, and tempering at a relatively low temperature.

1 近似對照表馬氏體不鏽鋼

中國		中國台灣	日本	韓國	美國		俄羅斯	瑞典	英國
GB	ISC	CNS	JIS	KS	ASTM	UNS	GOST	SS	BS EN/BS
12Cr12 (1Cr12)	S40310	403	SUS 403	STS 403	403	S40300	08Х13	2301	403S17

2 近似對照表馬氏體不鏽鋼

中國	日本	美國		德國	法國	歐标		俄羅斯	瑞典	英國
GB	JIS	ASTM	UNS	DIN EN/DIN	NF EN/NF	EN	數字牌号	GOST	SS	BS EN/BS
0Cr13	SUS410S	410S Type403	S41008	X7Cr14	Z6C13 Z8C12	X6Cr13	1.4000	08KH13	2301	403S17

材料牌号對應供應商

告訴我在“材數庫”看到，将給您優惠

上海亞螺精密緊固技術有限公司

主營: 各類不鏽鋼緊固件各類合金鋼緊固件特殊材質緊固件螺塞/堵頭耐高溫不鏽鋼緊固件 A4-80螺栓

聯系人：徐海
移動電話： 18621311857
電話：021-59766477
Email: 登陸後可見

詢價

江蘇德鎳金屬科技有限公司

主營: 奧氏體不鏽鋼馬氏體不鏽鋼沉澱硬化鋼雙相不鏽鋼高溫合金钛合金汽輪機鋼

聯系人：鄭經理
移動電話： 17365312205
微信号：17365312205
Email: 登陸後可見

闆材、薄闆、帶材、棒材、管材、型材等

詢價

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！