C25 - ISO 683-18-2014

牌号	C25
對應标準	ISO 683-18-2014 熱處理鋼、合金鋼和易切削鋼 -- 第18部分：光面鋼制品 Bright steel products
歸類	碳鋼

C25 化學元素成分含量(%)

成分	C	Si ^①	Mn	P	S	Cr	Ni	Cu	Mo	更多
最小值	0.22	0.1	0.4	-	-	-	-	-	-	Cr+Mo+Ni≤0.63
最大值	0.29	0.4	0.7	0.045	0.045	0.4	0.4	0.3	0.1	Cr+Mo+Ni≤0.63

① Steels may be supplied with a lower silicon content. In this case, alternative means of deoxidation shall be used.
② Steels with improved machinability either by higher sulfur levels up to about 0,10 % S (including controlled sulphide morphology) or lead additions may be available on request. In the first case, the upper limit of the Mn-content may be increased by 0,15 %.

碳當量計算

C25 機械性能

厚度 t mm	熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	硬度 HBW
5≤t≤10	Cold drawn (+C)	560~860	≥420	≥6
10＜t≤16	Cold drawn (+C)	530~830	≥380	≥7
16＜t≤40	Cold drawn (+C)	510~810	≥300	≥8
40＜t≤63	Cold drawn (+C)	490~790	≥265	≥9
63＜t≤100	Cold drawn (+C)	440~740	≥245	≥10
16＜t≤100	As-rolled + peeled (+SH)	440~640			131~187

1 近似對照表碳素結構鋼和工程用鋼

中國	日本	國際标準組織
GB	JIS	ISO
25	S25C	C25

2 近似對照表優質碳素結構鋼

中國	日本	美國	國際标準組織	德國		歐标		俄羅斯	瑞典	英國
GB	JIS	SAE	ISO	DIN EN/DIN	W-Nr.	EN	數字牌号	GOST	SS	BS EN/BS
20	S20C S22C	1020	C25	C22	1.0402	C22	1.0402	20	1450	070M20

3 近似對照表碳素結構鋼和工程用鋼

國際标準組織	德國	歐标		俄羅斯
ISO	DIN EN/DIN	EN	數字牌号	GOST
C25	C25	C25	1.0406	25

4 近似對照表優質碳素結構鋼

中國	日本	美國	國際标準組織	法國	俄羅斯	英國
GB	JIS	ASTM/AISI	ISO	NF EN/NF	GOST	BS EN/BS
GB/T 699-1999 25	S25C	1025	ISO 630-1:1987 C25 C25E4 C25M2	C25 XC25	25	060A25 070A26

C25 對應不同标準

1	ISO 683-18-1996 熱處理鋼、合金鋼和易切削鋼
	C25
2	DIN 17200-1987 調質鋼材的供貨技術條件
	C25 1.0406
3	EN 10250-2-2000 一般工程用自由鍛鋼鍛件.第2部分:非合金鋼和特種鋼
	C25 1.0406
4	ISO 683-1-2016 淬火和回火用非合金鋼
	C25
5	DIN EN ISO 683-1-2018 熱處理鋼、合金鋼和易切削鋼 -- 第1部分：調質非合金鋼
	C25
6	ISO 683-18-2014 熱處理鋼、合金鋼和易切削鋼 -- 第18部分：光面鋼制品
	C25