C40 - ISO 683-18-2014

牌号	C40
對應标準	ISO 683-18-2014 熱處理鋼、合金鋼和易切削鋼 -- 第18部分：光面鋼制品 Bright steel products
歸類	碳鋼

C40 化學元素成分含量(%)

成分	C	Si ^①	Mn	P	S	Cr	Ni	Cu	Mo	更多
最小值	0.37	0.1	0.5	-	-	-	-	-	-	Cr+Mo+Ni≤0.63
最大值	0.44	0.4	0.8	0.045	0.045	0.4	0.4	0.3	0.1	Cr+Mo+Ni≤0.63

① Steels may be supplied with a lower silicon content. In this case, alternative means of deoxidation shall be used.
② Steels with improved machinability either by higher sulfur levels up to about 0,10 % S (including controlled sulphide morphology) or lead additions may be available on request. In the first case, the upper limit of the Mn-content may be increased by 0,15 %.

碳當量計算

C40 機械性能

厚度 t mm	熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	硬度 HBW
5≤t≤10	Cold drawn (+C)	700~1000	≥540	≥6
10＜t≤16	Cold drawn (+C)	650~980	≥460	≥7
16＜t≤40	Cold drawn (+C)	620~920	≥365	≥8
40＜t≤63	Cold drawn (+C)	590~840	≥330	≥9
63＜t≤100	Cold drawn (+C)	550~820	≥290	≥9
16＜t≤100	As-rolled + peeled (+SH)	550~710			164~207

1 近似對照表碳素結構鋼和工程用鋼

中國	日本	國際标準組織	歐标
GB	JIS	ISO	EN	數字牌号
40	S40C	C40	C40	1.0511

2 近似對照表優質碳素結構鋼

中國	日本	美國	國際标準組織	德國		法國	歐标		俄羅斯	英國
GB	JIS	ASTM	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	EN	數字牌号	GOST	BS EN/BS
40	S40C	1038 1040	C40 C40E4	C40 Ck40	1.0511	AF60C40 AF60C45 XC42HI	C40	1.0511	40	070M40 080M40 En8

3 近似對照表優質碳素結構鋼

中國	日本	美國	國際标準組織	法國	俄羅斯	英國
GB	JIS	ASTM/AISI	ISO	NF EN/NF	GOST	BS EN/BS
GB/T 699-1999 40	S40C	1040	ISO 630-1:1987 C40 C40E4 C40M2	C42 XC42	40	060A40

C40 對應不同标準

1	ISO 683-18-1996 熱處理鋼、合金鋼和易切削鋼
	C40
2	DIN 17200-1987 調質鋼材的供貨技術條件
	C40 1.0511
3	EN 10083-2-2006 淬火和回火鋼.第2部分:非合金鋼交貨技術條件
	C40 1.0511
4	JIS G 7401-2000 冷鍛及冷軋擠壓用鋼
	(C40) 41CrNiMo2E
5	ISO 4954-1993 冷镦和冷擠壓用鋼
	(C40) 41CrNiMo2E
6	EN 10250-2-2000 一般工程用自由鍛鋼鍛件.第2部分:非合金鋼和特種鋼
	C40 1.0511
7	EN 10277-2-2008 光亮鋼制品.交貨技術條件.第2部分:一般工程用鋼
	C40 1.0511
8	ISO 683-1-2016 淬火和回火用非合金鋼
	C40
9	DIN EN ISO 683-1-2018 熱處理鋼、合金鋼和易切削鋼 -- 第1部分：調質非合金鋼
	C40
10	ISO 683-18-2014 熱處理鋼、合金鋼和易切削鋼 -- 第18部分：光面鋼制品
	C40
11	NF EN 10083-2-2006 調質非合金結構鋼
	C40 1.0511

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！