X20CrMoV11-1 1.4922 - EN 10222-2-2017

牌号	X20CrMoV11-1
歐标鋼号	1.4922
對應标準	EN 10222-2-2017 壓力用途用鋼制鍛件第2部分具有高溫特性的鐵素體和馬氏體鋼 Steel Forgings for Pressure Purposes. Part 2:Ferritic and Martensitic Steels with Specified Elevated Temperature Properties
歸類	合金鋼

X20CrMoV11-1 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Mo	V
最小值	0.17	-	0.3	-	-	10	0.3	0.8	0.2
最大值	0.23	0.4	1	0.02	0.005	12.5	0.8	1.2	0.35

碳當量計算

X20CrMoV11-1 機械性能

厚度 t mm	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	沖擊吸收能量 KV2 J
t≤100	750~850	≥500	I：≥16，tr/t：≥14	I：≥39，tr/t：≥27
100＜t≤250	750~850	≥500	I：≥16，tr/t：≥14	I：≥31，tr/t：≥27
250＜t≤330	750~850	≥500	I：≥16，tr/t：≥14	≥27

① I = longitudinal to main forging directions；tr = transverse to main forging directions；t = tangential.
② Maximum room temperature for the impact test is 20 °C. By option, impact testing may be carried out at 0°C, with the condition to fulfil the impact values as stated in this table.
③ Until the yield point criteria are harmonized in the various national codes, determination of ReH may be replaced by determination of Rp0.2. In this case Rp0.2 values are 10 MPa lower for ReH values up to 355 MPa and 15 MPa lower for ReH values greater than 355 MPa.

熱處理制度（僅供參考）

QT= quenched and tempered; a = air; f = furnaced; o = oil.

近似對照表馬氏體不鏽鋼

中國	德國	歐标
GB	DIN EN/DIN	EN	數字牌号
1Cr11MoV	X20CrMoV12-1 X22CrMoV12-1	X20CrMoV11-1	1.4922

材料牌号對應供應商

告訴我在“材數庫”看到，将給您優惠

上海日隆金屬制品有限公司

主營: 特鋼特材機械加工

聯系人：陳經理
移動電話： 13916390866

闆、棒、管、鍛件，盤圓、線材、絲材，帶箔材，來圖定制

詢價

X20CrMoV11-1 對應不同标準

1	EN 10088-1-2005 不鏽鋼第1部分:不鏽鋼的清單
	X20CrMoV 11-1 1.4922
2	EN 10216-2-2007 壓力無縫鋼管.交貨技術條件.規定高溫特性的非合金和合金鋼管
	X20CrMoV11-1 1.4922
3	EN 10302-2008 鎳和鎳钴合金的耐蠕變鋼
	X20CrMoV 11-1 1.4922
4	EN 10222-2-2017 壓力用途用鋼制鍛件第2部分具有高溫特性的鐵素體和馬氏體鋼
	X20CrMoV11-1 1.4922
5	NF EN 10216-2-2007 高溫用承壓無縫鋼管
	X20CrMoV11-1 1.4922
6	NF EN 10088-1-2005 不鏽鋼 - 第1部分：不鏽鋼清單
	X20CrMoV11-1 1.4922

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！

熱處理制度（僅供參考）

材料牌号對應供應商