AW2 - BS 3100-1991-材數庫

牌号	AW2
對應标準	BS 3100-1991 一般工程用鑄鋼件 Specification for Steel Castings for General Engineering Purposes
歸類	鑄鋼
标簽	碳鋼鑄鋼耐磨和表面硬化用鑄鋼

AW2 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr ^②	Ni ^②	Cu ^②	Mo ^②	其他合計
最小值	0.4	-	-	-	-	-	-	-	-	-
最大值	0.5	0.6	1	0.05	0.05	0.3	0.4	0.3	0.15	0.8

其他單個或其他合計化學成分包括表中未指定值的化學成分。隻有在假定存在或在常規分析中，且有迹象表明其成分将超過規定值的情況下，才應進行分析。

①碳含量每降低0.01%，最大錳含量則增加0.04%，允許最大錳含量到1.1%
②殘餘元素。

碳當量計算

AW2 機械性能

熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %
A或N或N+T	≥620	≥325	≥12

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

近似對照表鑄鋼

中國	日本	美國		國際标準組織	德國	俄羅斯	英國
GB	JIS	ASTM	UNS	ISO	DIN EN/DIN	GOST	BS EN/BS
ZG310-570	SCC5	80-40	J05002	340-550	GS-70 GS-CK45	45Л	A3 AW2

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！

版權說明：
⑴ 本網站的所有内容（包括但不限于文字、圖片、音頻、視頻等）均受到版權保護，版權歸本網站所有；
⑵ 未經授權，禁止以任何形式轉載、複制、傳播或用于其他商業用途；
⑶ 如需使用本網站内容，請提前獲得授權。

材料與專利鋼号免責聲明：
⑴ 本平台所收錄的部分材料牌号為企業專利鋼号或專有命名牌号，非 GB、ISO、DIN、ASTM、JIS 等通用标準鋼号；
⑵ 相關化學成分、力學性能及适用範圍以專利文件、權利人公開資料或供方技術文件為準；
⑶ 平台所展示信息僅用于材料檢索、工程參考及技術對比，不構成等同、替代或采購依據。