425C11 - BS 3100-1991

牌号	425C11
對應标準	BS 3100-1991 一般工程用鑄鋼件 Specification for Steel castings for general engineering purposes
歸類	鑄鋼
性能	耐腐蝕
标簽	不鏽鋼鑄鋼

425C11 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Mo
最小值	-	-	-	-	-	11.5	3.4	-
最大值	0.1	1	1	0.04	0.03	13.5	4.2	0.6

碳當量計算

425C11 機械性能

熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	沖擊吸收能量 KV2 J
AH或OQ(from 950°C to 1050°C)+T(590°C to 650°C)	≥770	≥620	≥12	≥30

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

近似對照表其他不鏽鋼

德國		法國	歐标		瑞典	英國
DIN EN/DIN	W-Nr.	NF EN/NF	EN	數字牌号	SS	BS EN/BS
X5CrNi 13-4	1.4313	Z25CN 13-4	X3CrNiMo 13-4	1.4313	2385	425C11

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！