347C17 - BS 3100-1991

牌号	347C17
對應标準	BS 3100-1991 一般工程用鑄鋼件 Specification for Steel castings for general engineering purposes
歸類	鑄鋼
性能	耐腐蝕
标簽	奧氏體不鏽鑄鋼有磁性

347C17 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	更多
最小值	-	-	-	-	-	18	9	Nb:8C~1
最大值	0.08	1.5	2	0.04	0.04	21	12	Nb:8C~1

碳當量計算

347C17 機械性能

熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %
ST(1000°C~1100°C)	≥480	1% proof stress Rp1.0 min ≥215	≥22

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

1 近似對照表耐蝕鑄鋼（不鏽鋼鑄件）

中國	日本	美國	德國		法國	英國
GB	JIS	ASTM	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
ZG0Cr18Ni9Ti	SUS21	CF8C	G-X7CrNiNb 18 9	1.4552	Z6CNNb18.10M	347C17

2 近似對照表耐熱鑄鋼和耐熱合金鑄件

中國	日本	美國		德國		法國	俄羅斯	英國
GB	JIS	ASTM	UNS	DIN EN/DIN	W-Nr.	NF EN/NF	GOST	BS EN/BS
ZG0Cr18Ni9Ti	SCS21	CF8C	J92710	G-X5CrNiNb18 9	1.4552	Z4CNNb19.10M	08Х18Н9Т	347C17