316C12 - BS 3100-1991

牌号	316C12
對應标準	BS 3100-1991 一般工程用鑄鋼件 Specification for Steel castings for general engineering purposes
歸類	鑄鋼
性能	耐腐蝕
标簽	奧氏體不鏽鑄鋼有磁性

316C12 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Mo
最小值	-	-	-	-	-	17	9	2
最大值	0.03	1.5	2	0.04	0.04	21	-	3

碳當量計算

316C12 機械性能

熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %
ST(1050°C~1150°C)	≥430	1% proof stress Rp1.0 min ≥215	≥26

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

近似對照表耐蝕鑄鋼（不鏽鋼鑄件）

中國		中國台灣	日本	韓國	美國		國際标準組織	德國	法國	英國
GB	ISC	CNS	JIS	KS	ASTM	UNS	ISO	DIN EN/DIN	NF EN/NF	BS EN/BS
ZG03Cr19Ni11Mo2	C53163	SCS 16A	SCS 16AX	SSC 16A	CF3M	J92800	GX2CrNiMo19-11-2	≈GX2CrNiNb19-11-2	Z2CND18.12M	316C12