330C11 - BS 3100-1991

牌号	330C11
對應标準	BS 3100-1991 一般工程用鑄鋼件 Specification for Steel castings for general engineering purposes
歸類	鑄鋼
性能	耐腐蝕
标簽	耐熱不鏽鑄鋼

330C11 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Mo
最小值	0.35	-	-	-	-	13	33	-
最大值	0.55	1.5	2	0.04	0.04	17	37	1.5

碳當量計算

330C11 機械性能

熱處理或狀态	抗拉強度 σ_b Mpa	斷後伸長率或延伸率 δ %
As cast	≥450	≥3

A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.

近似對照表耐熱鑄鋼和耐熱合金鑄件

中國		中國台灣	日本	韓國	美國		國際标準組織	德國		法國	英國
GB	ISC	CNS	JIS	KS	ASTM	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
ZG40Ni35Cr17Si2	C53931	SCH 15	SCH 15X	HRSC 15	HT	J94605	GX40NiCrSi35-17	GX40NiCrSi35-17	1.4806	GX40NiCrSi35-17	330C11

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！