E235 1.0308 - EN 10305-2-2002

牌号	E235
歐标鋼号	1.0308
對應标準	EN 10305-2-2002 精密儀器用鋼管.交貨技術條件.焊接冷拔鋼管 Steel tubes for precision applications - Technical delivery conditions - Welded cold drawn tubes
歸類	碳鋼

E235 化學元素成分含量(%)

成分	C	Si	Mn	P	S
最小值	-	-	-	-	-
最大值	0.17	0.35	1.2	0.025	0.025

①Elements not included in this Table (but see footnote *) shall not be intentionally added to the steel without the agreement of the purchaser, except for elements which may be added for finishing the cast. All appropriate measures shall be taken to prevent the addition of undesirable elements from scrap or other materials used in the steel making process.

碳當量計算

E235 機械性能

交貨狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %
+C	≥490	≥0.8σb	≥6
+LC	≥440	≥0.7σb	≥10
+SR	≥440	≥325	≥14
+A	≥315	≥0.5σb	≥25
+N	340~480	* ≥235	≥25

① +C=Cold drawn / hard(冷拔/硬化)；② +LC =Cold drawn / soft(冷拔/軟化)；③ +SR=Cold drawn and stress relieved(冷拔并去除應力)；④ +A=Annealed(退火)；⑤ +N=Normalized(正火)
*For tubes with outside diameter ≤ 30 mm and wall thickness ≤ 3 mm the ReH minimum values are 10 MPa lower than the values given in this Table.
注：表中σs為上屈服強度ReH

近似對照表優質碳素結構鋼

德國	法國	歐标		英國
DIN EN/DIN	NF EN/NF	EN	數字牌号	BS EN/BS
RSt37-2 St35	ES235 TS-34a TU376	E235	1.0308	CEW4 CFS4 ERW2 ERW3 ERW4

E235 對應不同标準

1	EN 10296-1-2003 機械和一般工程用焊接圓鋼管.技術交貨條件.非合金和合金鋼管
	E235 1.0308
2	EN 10297-1-2003 機械和通用無縫鋼管交貨技術條件第1部分:非合金和合金鋼管
	E235 1.0308
3	EN 10305-2-2002 精密儀器用鋼管.交貨技術條件.焊接冷拔鋼管
	E235 1.0308
4	EN 10305-1-2010 精密鋼管交貨技術條件第1部分冷拉無縫鋼管
	E235 1.0308

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！