X15CrMo5-1 1.7390 - NF EN 10269-1999

牌号	X15CrMo5-1
	1.7390
對應标準	NF EN 10269-1999 用于高溫或低溫條件下的緊固件用鋼及鎳合金
歸類	合金鋼
标簽	淬火回火鋼

X15CrMo5-1 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Mo
最小值	-	-	0.3	-	-	4	0.45
最大值	0.18	0.4	0.8	0.025	0.015	6	0.65

◎ 未經買方同意，不得随意向鋼中添加表中未列的元素，冶煉精加工除外。采用一切必要措施以防在廢鋼和生產原料中帶入這些元素，因為其會削弱鋼的機械性能，降低鋼的适用性

碳當量計算

X15CrMo5-1 機械性能

直徑 d mm	熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	斷面收縮率 ψ %	沖擊吸收能量 KV2 J
d≤160	+NT or +QT	640~780	≥420	≥14	≥45	≥40

◎ +AT=固溶退火；+C=冷作硬化；+N=正火；+NT=正火及回火；+P=沉澱硬化；+QT=淬火及回火；WW=熱作硬化；+AC=球化退火；+A=軟化退火；+S=冷剪處理（treated for cold shearing）

鋼在室溫和20攝氏度交貨條件下的機械性能，符合97/23/EC的基本安全要求

交付條件下在高溫下的最小屈服強度

Material designation		Heat treatment condition	Diameter d mm	Minimum 0.2%-proof strength R_p0.2 in MPa at a temperature (in°C) of:
Name	Number	Heat treatment condition	Diameter d mm	50	100	150	200	250	300	350	400	450	500	550	600	650
X15CrMo5-1	1.7390	+NT or +QT	d≤160	392	345	335	327	323	322	316	306	285	256	-	-	-

符合本歐洲标準的產品熱處理指南

Material designation		Heat treatment condition	Normalizing,quenching or solution annealing temperature °C	Type of cooling^①	Tempering or precipitation treatment (and time) °C
Name	Number
X15CrMo5-1	1.7390	+NT	925 to 975	a	690 to 750
		+QT	925 to 975	o	690 to 750

◎ 根據原件相關規定，如果允許矯直後消除應力，應選擇消除應力的溫度，以獲得規定的性能。
① a=air; o=oil; w=water

蠕變性能

Designation		Temperature	Strength for 1% (plastic) creep strain ①		Creep rupture strength for ②
Name	Number	°C	10000h	100000h	10000h	100000h	200000h
X15CrMo5-1	1.7390	450	-	-	-	276	237
		460	-	-	-	218	192
		470	-	-	226	181	158
		480	-	-	220	153	135
		490	88	63	190	132	114
		500	85	61	164	113	96
		510	76	54	145	96	80
		520	67	47	129	81	68
		530	60	42	114	70	57
		540	55	37	100	59	47
		550	49	32	88	50	40
		560	43	30	77	43	-
		570	37	26	68	37	-
		580	-	-	60	-	-
		590	-	-	53	-	-
		600	-	-	46	-	-

◎ The values given in this table are the mean values of the scatter band so far obtained, which will be checked from time to time as further test results become available and if necessary corrected.
◎ * and () indicate values of extended stress extrapolation or time extrapolation, respectively.
① This is the stress relative to the initial cross- section leadina to a permanent elongation of 1 % after 10000 h and 100000 h.
② This is the stress relative to the initial cross- section leading to fracture after 10000 h, 100000 h and 200000 h.

X15CrMo5-1 對應不同标準

1	EN 10269-2006 規定高溫和/或低溫性能的緊固件用鋼和鎳合金
	X15CrMo5-1 1.7390
2	EN 10269-2013 規定高溫和/或低溫性能的緊固件用鋼和鎳合金
	X15CrMo 5-1 1.7390
3	NF EN 10269-1999 用于高溫或低溫條件下的緊固件用鋼及鎳合金
	X15CrMo5-1 1.7390
4	DIN EN 10269-2014 規定高溫和/或低溫性能的緊固件用鋼和鎳合金
	X15CrMo 5-1 1.7390

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！