X8CrMnCuNB17-8-3 1.4597 - NF EN 10088-2-2005

牌号	X8CrMnCuNB17-8-3
	1.4597
對應标準	NF EN 10088-2-2005 普通用途不鏽鋼闆和鋼帶的交貨技術條件 Part2:Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
歸類	奧氏體不鏽鋼
标簽	特殊等級

X8CrMnCuNB17-8-3 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	N	B
最小值	-	-	6.5	-	-	16	-	2	-	0.15	0.0005
最大值	0.1	2	8.5	0.04	0.03	18	2	3.5	1	0.3	0.005

◎ 未經買方同意，不得随意向鋼中添加表中未列的元素，冶煉精加工除外。采取一切必要措施以防在廢鋼和生產原料中帶入這些元素，因為其會削弱鋼的機械性能，降低鋼的适用性。

◎ 在詢價和訂購時可商定更嚴格的碳含量範圍。

碳當量計算

X8CrMnCuNB17-8-3 機械性能

條件	熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	沖擊吸收能量 KV2 J
冷軋帶鋼：T ≤ 8mm	+AT	580~780	( t ) Rp0.2：≥ 300①③ Rp1.0：≥ 330①② ③	( t ) T＜3mm：≥40③④ T ≥ 3mm：≥40③⑤	-
熱軋帶鋼：T ≤ 13.5mm	+AT	580~780	( t ) Rp0.2：≥ 300①③ Rp1.0：≥ 330①② ③	( t ) T＜3mm：≥40③④ T ≥ 3mm：≥40③⑤	（T＞10mm） I：≥ 100；t：≥60
鋼材（工藝流程2H）：	冷加工+C700⑥⑦	700~850
鋼材（工藝流程2H）：	冷加工+C850⑥⑦	850~1000
鋼材（工藝流程2H）：	冷加工+C1000⑥⑦	1000~1150
鋼材（工藝流程2H）：	冷加工+CP350⑥⑦		350~500
鋼材（工藝流程2H）：	冷加工+CP500⑥⑦		500~700
鋼材（工藝流程2H）：	冷加工+CP700⑥⑦		700~900

◎ T-厚度；l-縱向; t-橫向
◎ +A=軟化退火；+QT=淬火及回火；+P=沉澱硬化；+AT=固溶退火；+SR=消除應力

① 對于連續熱軋產品，可在詢價和訂購時商定Rp0.2(即表中σs)的最小值提高20MPa，Rp1.0的最小值提高10MPa。
② 僅作指導
③ 如果在軋制寬度<300mm的情況下，采用縱向試驗件，最小值減小如下:屈服強度-15MPa，恒定标距的延伸率-5%，比例标距延伸率-2%。
④ T＜3mm時适用于标距為80mm、寬度為20mm的試件。也可以使用标距為50mm、寬度為12.5mm的試件。
⑤ T ≥3mm時适用于标距為5.65√S的試件。
⑥ 可商定中間抗拉強度和屈服強度值。另外可以指定鋼最小0.2%-耐強度或硬度，但訂單中隻能指定一個參數。
⑦ 每個抗拉強度和屈服強度等級的最大產品厚度随着抗拉強度的增大而減小。最大產品厚度和剩餘延伸率也取決于鋼的加工硬化行為和冷加工條件。因此，可能要求制造商提供更準确的信息。
* 交貨條件下有抗晶間腐蝕; 緻敏條件下無抗晶間腐蝕（根據EN ISO 3651-2進行測試）。

交付條件下在高溫下的最小屈服強度

Material designation		Heat treatment condition	Minimum 0.2%-proof strength,MPa at a temperature (in°C) of:										Minimum 1%-proof strength,MPa at a temperature (in°C) of:
Name	Number	Heat treatment condition	100	150	200	250	300	350	400	450	500	550	100	150	200	250	300	350	400	450	500	550
X8CrMnCuNB17-8-3	1.4597	+AT	225	205	190	177	165	152	145	140	137	135	260	235	218	204	190	180	175	168	165	165

符合本歐洲标準的產品熱處理指南

Material designation		Hot forming		Heat treatment symbol	Solution anneailing
Name	Number	Temperature ℃	Type of cooling	Heat treatment symbol	Temperature①②③ ℃	Type of cooling④
X8CrMnCuNB17-8-3	1.4597	1150 to 850	air	+AT	1000 to 1100	water,air

◎ Temperature of solution annealing shall be agreed for simulated heat-treated test pieces.
① Solution annealing may be omitted if the conditions for hot working and subsequent cooling are such that the requirements for the mechanical properties of the product and the resistance to intergranular corrosion as defined in EN ISO 3651-2 are obtained.
② If heat treatment is carried out in a continuous furnace, the upper part of the range specified is usually preferred, or even exceeded.
③ Lower end of the range specified for solution annealing should be aimed at the heat treatment as part of further processing,because otherwise the mechanical properties might be affected. If the temperature of hot forming does not drop below the lower temperature for solution annealing, a temperature of 980℃ is adequate as a lower limit for Mo-free steels, a temperature of 1000℃ for steels with Mocontents up to 3 % and a temperature of 1020°C for steels with Mo contents exceeding 3 %.
④ Cooling sufficiently rapidly in order to avoid the occurrence of intergranular corrosion as defined in EN ISO 3651-2.

X8CrMnCuNB17-8-3 對應不同标準

1	EN 10088-1-2005 不鏽鋼第1部分:不鏽鋼的清單
	X8CrMnCuNB 17-8-3 1.4597
2	NF EN 10088-2-2005 普通用途不鏽鋼闆和鋼帶的交貨技術條件
	X8CrMnCuNB17-8-3 1.4597
3	NF EN 10088-1-2005 不鏽鋼 - 第1部分：不鏽鋼清單
	X8CrMnCuNB17-8-3 1.4597

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！