S275N 1.0490 - EN 10025-3-2004

牌号	S275N
歐标鋼号	1.0490
對應标準	EN 10025-3-2004 熱軋結構鋼鋼材第3部分：正火/正火軋制可焊接的細晶結構鋼 Hot rolled products of structural steels - Part 3: Technical delivery conditions for normalized/normalized rolled weldable fine grain structural steels
歸類	碳鋼

S275N 化學元素成分含量(%)

成分	C	Si	Mn	P ^①	S ^①②	Cr	Ni	Cu ^④	Mo	N	Ti	V	Nb	Al ^③
最小值	-	-	0.5	-	-	-	-	-	-	-	-	-	-	0.02
最大值	0.18	0.4	1.5	0.03	0.025	0.3	0.3	0.55	0.1	0.015	0.05	0.05	0.05	-

① For long products the P and S content can be 0.005% higher.
② For railway applications a maximum S content of 0.010% may be agreed at the time of enquiry and order.
③ If sufficient other N-binding elements are present the minimum total Al content does not apply.
④ Cu content above 0.40% may cause hot shortness during hot forming.

S275N 機械性能

公稱厚度 t mm	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %
t≤16	370~510	≥275	≥24
16<t≤40	370~510	≥265	≥24
40<t≤63	370~510	≥255	≥24
63<t≤80	370~510	≥245	≥23
80<t≤100	370~510	≥235	≥23
100<t≤150	350~480	≥225	≥23
150<t≤200	350~480	≥215	≥23
200<t≤250	350~480	≥205	≥23

For plate,strip and wide flats with widths≥600mm the direction transverse (t) to the rolling direction applies. For all other products the values apply for the direction parallel (l) to the rolling direction

①在此測試溫度下的最小沖擊吸收能量

1 近似對照表優質碳素結構鋼

日本	美國	德國		歐标		英國
JIS	ASTM	DIN EN/DIN	W-Nr.	EN	數字牌号	BS EN/BS
SM400B	A572Gr.42 A633A	StE285	1.0486	S275N FeE275KGN①	1.0490	43DD

S275N 對應不同标準

1	EN 10025-3-2004 熱軋結構鋼鋼材第3部分：正火/正火軋制可焊接的細晶結構鋼
	S275N 1.0490
2	EN 10025-3-2019 正火/正火軋制可焊細粒結構鋼
	S275N 1.0490

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！