S275NL 1.0491 - EN 10025-3-2004

牌号	S275NL
歐标鋼号	1.0491
對應标準	EN 10025-3-2004 熱軋結構鋼鋼材第3部分：正火/正火軋制可焊接的細晶結構鋼 Hot rolled products of structural steels - Part 3: Technical delivery conditions for normalized/normalized rolled weldable fine grain structural steels
歸類	碳鋼

S275NL 化學元素成分含量(%)

成分	C	Si	Mn	P ^①	S ^①②	Cr	Ni	Cu ^④	Mo	N	Ti	V	Nb	Al ^③
最小值	-	-	0.5	-	-	-	-	-	-	-	-	-	-	0.02
最大值	0.16	0.4	1.5	0.025	0.02	0.3	0.3	0.55	0.1	0.015	0.05	0.05	0.05	-

① For long products the P and S content can be 0.005% higher.
② For railway applications a maximum S content of 0.010% may be agreed at the time of enquiry and order.
③ If sufficient other N-binding elements are present the minimum total Al content does not apply.
④ Cu content above 0.40% may cause hot shortness during hot forming.

S275NL 機械性能

公稱厚度 t mm	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %
t≤16	370~510	≥275	≥24
16<t≤40	370~510	≥265	≥24
40<t≤63	370~510	≥255	≥24
63<t≤80	370~510	≥245	≥23
80<t≤100	370~510	≥235	≥23
100<t≤150	350~480	≥225	≥23
150<t≤200	350~480	≥215	≥23
200<t≤250	350~480	≥205	≥23

For plate,strip and wide flats with widths≥600mm the direction transverse (t) to the rolling direction applies. For all other products the values apply for the direction parallel (l) to the rolling direction

近似對照表碳素結構鋼和工程用鋼

美國	德國	歐标		英國
ASTM	DIN EN/DIN	EN	數字牌号	BS EN/BS
A633Gr.A	TStE285	S275NL FeE275KTN①	1.0491	43EE

S275NL 對應不同标準

1	EN 10025-3-2004 熱軋結構鋼鋼材第3部分：正火/正火軋制可焊接的細晶結構鋼
	S275NL 1.0491
2	EN 10025-3-2019 正火/正火軋制可焊細粒結構鋼
	S275NL 1.0491

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！