牌号 X2CrNiMo17-12-3
1.4432
對應标準 NF EN 10028-7-2000
壓力容器用不鏽鋼扁平產品
Flat products made of steels for pressure purposes Part 7: Stainless steels
歸類 奧氏體不鏽鋼
标簽 标準等級
X2CrNiMo17-12-3 化學元素成分含量(%)
成分 C Si Mn P S Cr Ni Mo N
最小值 - - - - - 16.5 10.5 2.5 -
最大值 0.03 1 2 0.045 0.015 18.5 13 3 0.11
◎ 未經買方同意，不得随意向鋼中添加表中未列的元素，冶煉精加工除外。采取一切必要措施以防在廢鋼和生產原料中帶入這些元素，因為其會削弱鋼的機械性能，降低鋼的适用性。
碳當量計算
X2CrNiMo17-12-3 機械性能
條件 熱處理或狀态
抗拉強度
σb
Mpa 		屈服點
σs
Mpa 		斷後伸長率或延伸率
δ
% 		沖擊吸收能量
KV2
J
C：T ≤ 6 +AT 550~700 Rp0.2：≥240
Rp1.0：≥270
①②		 T ＜ 3mm: ≥40
T ≥ 3mm: ≥ 40
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
H：T ≤ 12 +AT 550~700 Rp0.2：≥220
Rp1.0：≥260
①②		 T ＜ 3mm: ≥40
T ≥ 3mm: ≥ 40
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
P：T ≤ 75 +AT 520~670 Rp0.2：≥220
Rp1.0：≥260
①②		 T ＜ 3mm: ≥45
T ≥ 3mm: ≥ 45
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
◎C- 冷軋帶鋼; H- 熱軋帶鋼; P- 熱軋中厚闆；T- 厚度；t- 橫向；l-縱向。
◎+A=軟化退火；+AT=固溶退火；+QT=淬火及回火；+RA=再結晶退火。
◎ 如果熱加工和随後冷卻的條件符合ENISO3651-2中對產品機械性能和抗晶間腐蝕性的要求，則可以省略固溶處理。
*抗晶間腐蝕根據EN ISO 3651-2進行測試。在交貨條件下：有；在緻敏狀态下：有。
① 對于連續熱軋產品，可在詢價和訂購時商定Rp0.2(即表中σs)的最小值提高20MPa，Rp1.0的最小值提高10MPa。
② 如果在軋制寬度<300mm的帶材情況下，采用縱向試驗件，最小值減小如下:抗拉強度-15MPa，恒定标距的延伸率-5%，比例标距延伸率-2%。
③ T＜3mm：該值适用于标距為80mm、寬度為20mm的試件，也可以使用标距為50mm、寬度為12.5mm的試件。T ≥3mm：該值适用于标距為5.65√S的試件。

  • 高溫下的最小屈服強度

    Material designationHeat treatment
    condition    		Minimum 0.2% proof strength Rp0.2,MPa
    at a temperature (in°C) of:
    Name Number100150200250300350400450500550600
    X2CrNiMo17-12-31.4432+AT16615213712711811310810310098-
    Minimum 1.0% proof strength Rp1.0,MPa
    at a temperature (in°C) of:
    100150200250300350400450500550600
    199181167157145139135130128127-

  • 高溫下的最小抗拉強度

    Material designationMinimum tensile strength Rm,MPa
    at a temperature (in°C) of:
    Name Number100150200250300350400450500550600
    X2CrNiMo17-12-31.4432430410390385380380380-360--

  • 熱處理指南

    Material designationHot formingHeat
    treatment
    symbol    		 Solution anneailing
    ①②    		Post weld heat 
    treatment
    Steel with ≤ 0.03% C
    Name NumberTemperature
    ℃    		Type of
    cooling    		Temperature
    ℃ ③④    		Type of
    cooling    		Temperature
    ℃ ⑥    		Type of
    cooling
    X2CrNiMo17-12-31.44321150 to 850air+AT1030 to 1110water,air ⑤960 to 1040 ⑦forced air 
    ◎ a=air; o=oil; w=water.
    ◎ Scale and annealing colours produced during hot forming, heat treatment or welding may adversely affect the corrosion resistance. They should be removed as far as possible before use, e.g. by pickling.
    ◎ The temperatures of annealing should be agreed for simulated heat treated test pieces.
    ① The solution treatment may be omitted if the conditions for hot working and subsequent cooling are such that the requirements for the mechanical properties of the product and the resistance to intergranular corrosion as defined in EN ISO 3651-2 are obtained and provided these requirements are met even after appropriate subsequent solution annealing.
    ② Re-crystallizing annealing.
    ③ If heat treatment is carried out in a continuous furnace, the upper part of the range specified is usually preferred, or even exceeded.
    ④ The lower end of the range specified for solution annealing should be aimed at for heat treatment as part of further processing,because otherwise the mechanical properties might be affected. If the temperature of hot forming does not drop below the lower temperature for solution annealing.a temperature of 980℃ is adequate as a lower limit for Mo-free steels,a temperature of 1000℃ for steels with Mo contents up to 3% and a temperature of 1020℃ for steets with Mo contents exceeding 3%.
    ⑤ cooling sufficiently rapid.

    ⑥ Minimum holding time:30min.

    ⑦ Not recommended if welded with stabilized filler medal.

X2CrNiMo17-12-3 對應不同标準
1 EN 10088-1-2005 不鏽鋼 第1部分:不鏽鋼的清單
X2CrNiMo 17-12-3 1.4432
2 EN 10296-2-2005 機械工程和一般工程用焊接圓鋼管.交貨技術條件.第2部分:不鏽鋼
X2CrNiMo17-12-3 1.4432
3 EN 10253-4-2003 對接焊管道接頭.具有特殊檢驗要求的鍛制奧氏體和鐵素體－奧氏體(二相)不鏽鋼
X2CrNiMo17-12-3 1.4432
4 EN 10263-5-2001 冷镦和冷擠壓鋼杆材、棒材和線材.第5部分:不鏽鋼交貨技術條件
X2CrNiMo17-12-3 1.4432
5 ISO TS 15510-2003 技術規範 不鏽鋼-化學成分
X2CrNiMo17-12-3
6 EN 10088-3-2014 不鏽鋼 - 第3部分：半成品，棒材，杆材，線材，型材和光亮產品的一般用途耐腐蝕鋼的交貨技術條件
X2CrNiMo17-12-3 1.4432
7 ISO 15510-2014 技術規範 不鏽鋼-化學成分
X2CrNiMo17-12-3 4432-316-03-I
8 DIN EN 10263-5-2018 冷镦和冷擠壓盤條、棒材、鋼絲 - 第5部分：不鏽鋼交貨技術條件
X2CrNiMo 17-12-3 1.4432
9 ISO 9328-7-2018 不鏽鋼承壓扁鋼制品
X2CrNiMo17-12-3
10 DIN EN 10088-3-2014 不鏽鋼-半成品、棒材、杆材、線材、型材及光亮產品交貨技術條件
X2CrNiMo17-12-3 1.4432
11 ISO 683-18-2014 熱處理鋼、合金鋼和易切削鋼 -- 第18部分：光面鋼制品
X2CrNiMo17-12-3 4432-316-03-I
12 ISO 4954-2018 冷镦和冷擠壓用鋼
X2CrNiMo17-12-3 4432-316-03-I
13 NF EN 10088-2-2005 普通用途不鏽鋼闆和鋼帶的交貨技術條件
X2CrNiMo17-12-3 1.4432
14 NF EN 10088-1-2005 不鏽鋼 - 第1部分：不鏽鋼清單
X2CrNiMo17-12-3 1.4432
15 NF EN 10028-7-2008 壓力容器用不鏽鋼扁平產品
X2CrNiMo17-12-3 1.4432
16 NF EN 10296-2-2005 機械和一般工程用焊接圓鋼管-交貨技術條件-第2部分:不鏽鋼管
X2CrNiMo17-12-3 1.4432
17 NF EN 10028-7-2000 壓力容器用不鏽鋼扁平產品
X2CrNiMo17-12-3 1.4432
18 EN 10263-5-2017 冷镦和冷擠壓盤條、棒材、鋼絲 - 第5部分：不鏽鋼交貨技術條件
X2CrNiMo 17-12-3 1.4432
19 ISO 4954-2-2024 冷镦及冷擠壓鋼交貨技術條件 第2部分：不鏽鋼
X2CrNiMo17-12-3 4432-316-03-I
注：數據僅供參考！如有疑問，請填寫"我要糾錯"！