GX40CrNiSi22-9 1.4826 - DIN 17465-1993

牌号	GX40CrNiSi22-9
德國W-Nr.	1.4826
對應标準	DIN 17465-1993 耐熱鑄鋼 Heat resisting steel castings - Technical delivery conditions
歸類	鑄鋼
标簽	奧氏體型耐熱鑄鋼最高工作溫度950°C

GX40CrNiSi22-9 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni
最小值	0.3	1	-	-	-	21	9
最大值	0.5	2.5	1.5	0.035	0.03	23	11

碳當量計算

GX40CrNiSi22-9 機械性能

產品	熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	硬度 HBW
鑄鋼；t≤25	鑄态	≥440①	≥230	≥8①	-

①适用于厚度t≤25mm的產品

高溫性能及最高使用溫度

Material 1% creep limit after 10000 h, in N/mm²,
at a temperature, in °C, of Maximum service
temperature,
in °C
designation number 600 700 800 900 1000 1100
GX40CrNiSi22-9 1.4826 82 46 23 10 - - 950

物理性能

Material		Den- sity, in g/cm³	Thermal con- ductivity, in W/K.m	Specific heat capacity at 20 °C, in J/g.K	Coefficient of linear thermal expansion, in 10^-6 /K, at a temperature between 20 °C and
designation	number	Den- sity, in g/cm³	Thermal con- ductivity, in W/K.m	Specific heat capacity at 20 °C, in J/g.K	400 °C	800°C	1000°c
GX40CrNiSi22-9	1.4826	7.8	14.6	0.50	17.5	18.5	19.5

焊接資料

Material

suitable fillet metal

Heat treatment

designation

number

Covered electrode (symbol)

Wire or rod
(symbol)

Material number

prior to welding

after welding

GX40CrNiSi22-9

1.4826

22 12

25 20hC*

X12CrNi22-12 X40CN25-21

1.4829

1.4846

不預熱或隻稍微預熱(到摸起來溫暖)。

不需熱處理

*hC表示高含碳量

近似對照表耐熱鑄鋼和耐熱合金鑄件

中國

中國台灣

日本

韓國

美國

國際标準組織

德國

法國

俄羅斯

英國

ISC

CNS

JIS

ASTM

UNS

ISO

DIN EN/DIN

W-Nr.

NF EN/NF

GOST

BS EN/BS

ZG40Cr22Ni10Si2

C53871

≈SCH 12

SCH 12X

≈HRSC 12

J92603

GX40CrNiSi22-10

GX40CrNiSi20-9

1.4826

GX40CrNiSi22-10

40Х24Н12СЛ

GX40CrNiSi22-10

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！

Material		1% creep limit after 10000 h, in N/mm², at a temperature, in °C, of						Maximum service temperature, in °C
designation	number	600	700	800	900	1000	1100	Maximum service temperature, in °C
GX40CrNiSi22-9	1.4826	82	46	23	10	-	-	950

高溫性能及最高使用溫度

物理性能

焊接資料