GX40NiCrSi35-25 1.4857 - DIN 17465-1993 - 材數庫

簡體中文 | English

牌号	GX40NiCrSi35-25
德國W-Nr.	1.4857
對應标準	DIN 17465-1993 耐熱鑄鋼 Heat Resisting Steel Castings - Technical Delivery Conditions
歸類	鑄鋼
标簽	奧氏體型耐熱鑄鋼最高工作溫度1100°C

GX40NiCrSi35-25 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni
最小值	0.3	1	-	-	-	24	34
最大值	0.5	2.5	1.5	0.035	0.03	26	36

碳當量計算

GX40NiCrSi35-25 機械性能

產品	熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	硬度 HBW
鑄鋼	鑄态	≥440①	≥230	≥5①	-

①适用于厚度t≤25mm的產品

高溫性能及最高使用溫度

Material 1% creep limit after 10000 h, in N/mm²,
at a temperature, in °C, of Maximum service
temperature,
in °C
designation number 600 700 800 900 1000 1100
GX40NiCrSi35-25 1.4857 - 70 40 20 8 2 1100

物理性能

Material		Den- sity, in g/cm³	Thermal con- ductivity, in W/K.m	Specific heat capacity at 20 °C, in J/g.K	Coefficient of linear thermal expansion, in 10^-6 /K, at a temperature between 20 °C and
designation	number	Den- sity, in g/cm³	Thermal con- ductivity, in W/K.m	Specific heat capacity at 20 °C, in J/g.K	400 °C	800°C	1000°c
GX40NiCrSi35-25	1.4857	8	14.6	0.50	15.5	17.0	18.0

焊接資料

Material suitable fillet metal Heat treatment
designation number Covered
electrode
(symbol) Wire or rod
(symbol) Material number prior to welding after welding
GX40NiCrSi35-25 1.4857 25 35Nb X40NiCrNb35-25 1.4853 - -

1 近似對照表耐熱鑄鋼和耐熱合金鑄件

中國		中國台灣	日本	韓國	美國		國際标準組織	德國		法國	英國
GB	ISC	CNS	JIS	KS	ASTM	UNS	ISO	DIN EN/DIN	W-Nr.	NF EN/NF	BS EN/BS
ZG40Ni35Cr26Si2	C53941	SCH 24	SCH 24X	HRSC 24	HP	J95705	GX40NiCrSi35-26	GX40NiCrSi35-25	1.4857	GX40NiCrSi35-26	GX40NiCrSi35-26

2 近似對照表耐蝕鑄鋼（不鏽鋼鑄件）

中國	美國	德國
GB	ASTM	DIN EN/DIN	W-Nr.
ZG4Cr25Ni35Si2	HP	G-X45NiCrSi35 25	1.4857

3 近似對照表耐熱鑄鋼和耐熱合金鑄件

中國	日本	美國		德國
GB	JIS	ASTM	UNS	DIN EN/DIN	W-Nr.
ZG4Cr25Ni35Si2	SCH24	HP	J95705	G-X45CrNiSi35 25	1.4857

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！