牌号	G-CoCr28
德國W-Nr.	2.4778
對應标準	DIN 17465-1993 耐熱鑄鋼 Heat resisting steel castings - Technical delivery conditions
歸類	鑄鋼
标簽	奧氏體型耐熱鑄鋼最高工作溫度1100°C

G-CoCr28 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Co
最小值	0.1	0.5	-	-	-	27	48
最大值	0.2	1.5	1.5	0.035	0.03	30	52

G-CoCr28 機械性能

產品	熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	硬度 HBW
鑄鋼	鑄态	-	-	-	-

高溫性能及最高使用溫度

Material 1% creep limit after 10000 h, in N/mm²,
at a temperature, in °C, of Maximum service
temperature,
in °C
designation number 600 700 800 900 1000 1100
G-CoCr 28 2.4778 - 70 34 16 6 - 1100

物理性能

Material		Den- sity, in g/cm³	Thermal con- ductivity, in W/K.m	Specific heat capacity at 20 °C, in J/g.K	Coefficient of linear thermal expansion, in 10^-6 /K, at a temperature between 20 °C and
designation	number	Den- sity, in g/cm³	Thermal con- ductivity, in W/K.m	Specific heat capacity at 20 °C, in J/g.K	400 °C	800°C	1000°c
G-CoCr 28	2.4778	8.1	9.2	0.50	15.5	17.0	18

焊接資料

Material suitable fillet metal Heat treatment
designation number
Covered
electrode
(symbol)
Wire or rod
(symbol)
Material
number
prior to welding after welding
G-CoCr 28 2.4778 G-CoCr 28
-
2.4778 - -

G-CoCr28 對應不同标準

1	EN 10295-2002 耐熱鋼鑄件
	G-CoCr28 2.4778
2	DIN 17465-1993 耐熱鑄鋼
	G-CoCr28 2.4778