基本信息
牌号 F436 Type 1
對應标準 ASTM F436/436M-2024
淬火鋼墊圈的标準規範
Standard Specification for Hardened Steel Washers Inch and Metric Dimensions
類别 碳鋼
化學成分
F436 Type 1 化學元素成分含量(%)
  成分 P S
Heat analysis 最小值 - -
最大值 0.04 0.05
  成分 P S
Product analysis 最小值 - -
最大值 0.05 0.06
碳當量計算
機械性能
F436 Type 1 機械性能
硬度
HBW
Through hardened washers HRC
38~45
zinc-coated by the hot-dip HRC
26~45
① Through hardened washers shall have a hardness of 38 to 45 HRC, except when zinc-coated by the hot-dip process, in which case they shall have a hardness of 26 to 45 HRC.
② Carburized washers shall be carburized to a minimum depth of 0.015 in. (inch series) or 0.38 mm (metric series) and shall have a surface hardness of 69 to 73 HRA or 79 to 83 HR15N, except when zinc-coated by the hot-dip process, in which case they shall have a hardness of 63 to 73 HRA or 73 to 83 HR15N.
③ Carburized and hardened washers shall have a minimum core hardness of 30 HRC or 65 HRA.
F436 Type 1 對應标準的曆史替代
ASTM F436/436M - 2016 ASTM F436/436M - 2019 ASTM F436/436M - 2024
同名标準
F436 Type 1 對應不同标準
1
ASTM F436/436M-2016 淬火鋼墊圈的标準規範
F436 Type 1
2
ASTM F436/436M-2019 淬火鋼墊圈的标準規範
F436 Type 1
3
ASTM F436/436M-2024 淬火鋼墊圈的标準規範
F436 Type 1
注：數據僅供參考！如有疑問，請填寫"我要糾錯"！
版權說明：
⑴ 本網站的所有内容（包括但不限于文字、圖片、音頻、視頻等）均受到版權保護，版權歸本網站所有；
⑵ 未經授權，禁止以任何形式轉載、複制、傳播或用于其他商業用途；
⑶ 如需使用本網站内容，請提前獲得授權。

材料與專利鋼号免責聲明：
⑴ 本平台所收錄的部分材料牌号為企業專利鋼号或專有命名牌号，非 GB、ISO、DIN、ASTM、JIS 等通用标準鋼号；
⑵ 相關化學成分、力學性能及适用範圍以專利文件、權利人公開資料或供方技術文件為準；
⑶ 平台所展示信息僅用于材料檢索、工程參考及技術對比，不構成等同、替代或采購依據。
摘要 / Summary
F436 Type 1 材料牌号數據，對應标準：ASTM F436/436M-2024，主要化學成分：P ≤0.04%，P ≤0.05%，S ≤0.05%，S ≤0.06%，材數庫提供該材料的基本信息、化學成分、性能數據、相關标準及認證供應商參考信息，本頁面展示的供應商為材數庫認證供應商，企業資料由企業提交并經材數庫審核後發布。數據來源：材數庫 Caishuku.com。
推薦引用：材數庫 Caishuku Material Database， 《F436 Type 1 材料牌号數據》， https://www.caishuku.com/material/detail.php?mid=azhlNWIxMzExNzA=
F436 Type 1 的供應商信息由材數庫認證企業提供。 本頁面展示的企業均為材數庫認證供應商， 企業名稱、聯系人、聯系方式、 主營產品及供貨信息由企業提交， 經材數庫審核後發布并持續維護。
對比 0