F593 416 S41600 - ASTM F593-2017

牌号	F593 416
美國UNS	S41600
對應标準	ASTM F593-2017 不鏽鋼螺栓、六角螺釘和螺柱标準規範 Standard specification for stainless steel bolts, hex cap screws, and studs
歸類	馬氏體不鏽鋼

F593 416 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Mo ^①
最小值	-	-	-	-	0.15	12	-
最大值	0.15	1	1.25	0.06	-	14	0.6

① 由制造商選擇添加元素。

碳當量計算

F593 416 機械性能

公稱直徑 inch 試樣	熱處理或狀态	抗拉強度 σ_b ksi	屈服點 σ_s ksi	斷後伸長率或延伸率 δ %	硬度 HBW
1/4 ~ 1-1/2 (全尺寸)	H	110~140	≥90		HR (C20~30)
1/4 ~ 1-1/2 (全尺寸)	HT	160~190	≥120		HR (C34~45)
1/4 ~ 1-1/2 (機加工)	H	≥110	≥90	≥18
1/4 ~ 1-1/2 (機加工)	HT	≥160	≥120	≥12

注1： “全尺寸”指的拉力測試試件是使用前的狀态未經改變的完整的緊固件產品。
注2：A——Machined from annealed or solution-annealed stock thus retaining the properties of the original material, or hot-formed and solution-annealed.
AF——Headed and rolled from annealed stock and then reannealed.
AH——Solution annealed and age-hardened after forming.
CW——Headed and rolled from annealed stock thus acquining a degree of cold work; sizes 0.75 in. and larger may be hot worked and solution-annealed.
H——Hardened and tempered at 1050°F (565℃) minimum.
HT——Hardened and tempered at 525°F (274℃) minimum.
SH——Machined from strain hardened stock or cold-worked to develop the specified properties.

近似對照表馬氏體不鏽鋼

中國

中國台灣

日本

韓國

美國

國際标準組織

德國

法國

歐标

瑞典

英國

ISC

CNS

JIS

ASTM

UNS

ISO

數字牌号

DIN EN/DIN

W-Nr.

NF EN/NF

數字牌号

BS EN/BS

Y12Cr13
(Y1Cr13)

S41617

416

SUS 416

STS 416

416

S41600

X12CrS 13

4005-416-00-I

X12CrS 13

1.4005

Z12CF 13
Z11CF13

X12CrS 13

1.4005

2380

416S21

材料牌号對應供應商

告訴我在“材數庫”看到，将給您優惠

江蘇德鎳金屬科技有限公司

主營: 奧氏體不鏽鋼馬氏體不鏽鋼沉澱硬化鋼雙相不鏽鋼高溫合金钛合金汽輪機鋼

聯系人：鄭經理
移動電話： 17365312205
微信号：17365312205
Email: 登陸後可見

闆材、薄闆、帶材、棒材、管材、型材等

詢價

上海三富金屬集團有限公司

主營: 冷镦線材特殊鋼鋼帶合金鋼模具鋼軸承鋼彈簧鋼齒輪鋼冷墩鋼冷拉鋼

聯系人：林先生
移動電話： 13818300616/18601636665
電話：021-67600511/67600335
微信号：13818300616/18601636665
Email: 登陸後可見

鋼棒、鋼線、鋼管、鋼闆、鋼帶、異形等

詢價

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！