A871 Grade 60 - ASTM A871/A871M-2014

牌号	A871 Grade 60
對應标準	ASTM A871/A871M-2014 耐大氣腐蝕的高強度低合金結構鋼闆 High-Strength Low-Alloy Structural Steel Plate With Atmospheric Corrosion Resistance
歸類	合金鋼

A871 Grade 60 化學元素成分含量(%)

	成分	C ^①	Si	Mn ^①	P	S	Cr	Ni	Cu	V
Type Ⅰ	最小值	-	0.3	0.8	-	-	0.4	-	0.25	0.02
Type Ⅰ	最大值	0.19	0.65	1.35	0.03	0.03	0.7	0.4	0.4	0.1

	成分	C ^①	Si	Mn ^①	P	S	Cr	Ni	Cu	V
Type Ⅱ	最小值	-	0.15	0.75	-	-	0.4	-	0.2	0.01
Type Ⅱ	最大值	0.2	0.5	1.35	0.03	0.03	0.7	0.5	0.4	0.1

	成分	C ^①	Si	Mn ^①	P	S	Cr	Ni	Cu	Mo	Nb ^②
Type Ⅳ	最小值	-	0.25	0.5	-	-	0.4	-	0.3	-	0.005
Type Ⅳ	最大值	0.17	0.5	1.2	0.03	0.03	0.7	0.4	0.5	0.1	0.05

① For each reduction of 0.01 percentage point below the specified maximum for carbon, an increase of 0.06 percentage point above the specified maximum for manganese is permitted, up to a maximum of 1.50 %.
② For plates under 1/2 in. (13 mm) in thickness, the minimum columbium is waived.

碳當量計算

A871 Grade 60 機械性能

抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %
≥520	≥415	(50mm) ≥18

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！