S46910 - ASTM A693-2013-材數庫

美國UNS	S46910
對應标準	ASTM A693-2013 沉澱硬化不鏽鋼和耐熱鋼闆、薄闆和帶材 Precipitation-Hardening Stainless and Heat-Resisting Steel Plate, Sheet, and Strip
歸類	沉澱硬化型不鏽鋼

化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	Ti	Al
最小值	-	-	-	-	-	11	8	1.5	3	0.5	0.15
最大值	0.03	0.7	1	0.03	0.015	13	10	3.5	5	1.2	0.5

碳當量計算

機械性能

厚度 t mm	熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	硬度 HBW
0.02＜t＜3.8	Cold rolled at mill	≥950	≥475	≥5	HRC ≥29
0.02＜t＜3.8	Cold rolled at mill +475℃	≥1250	≥950	≥1	HRC ≥38
0.015＜t＜2.3	Cold rolled at mill	≥1100	≥650	≥3	HRC ≥33
0.015＜t＜2.3	Cold rolled at mill +475℃	≥1650	≥1450	≥1	HRC ≥46
0.015＜t＜1.2	Cold rolled at mill	≥1300	≥1100	≥1	HRC ≥38
0.015＜t＜1.2	Cold rolled at mill +475℃	≥1950	≥1850		HRC ≥50
0.015＜t＜0.7	Cold rolled at mill	≥1500	≥1350		HRC ≥42
0.015＜t＜0.7	Cold rolled at mill +475℃	≥2250	≥2150		HRC ≥54
0.015＜t＜0.15	Cold rolled at mill	≥1700	≥1525		HRC ≥45
0.015＜t＜0.15	Cold rolled at mill +475℃	≥2350	≥2250		HRC ≥55

① Furnished in cold-worked condition. Precipitation Hardening Treatment：475 + 8℃, 4 h, air cool.
注：Reduction of Area：Applicable to tests in the long transverse direction. Transverse to the direction of rolling and parallel to the product surface.

近似對照表沉澱硬化型不鏽鋼

中國		美國	國際标準組織		歐标
GB	ISC	UNS	ISO	數字牌号	數字牌号
022Cr12Ni9Mo4Cu2AlTi GB/T 20878-2024	S51293	S46910 ASTM A959	X2CrNiMoCuAlTi12-9-4-3 ISO 15510	4645-469-10-U	(1.4645)

材料牌号對應供應商

告訴我在“材數庫”看到，将給您優惠

江油市龍海特鋼有限公司

主營: GJB HB GB,GB/T DL/T YB/T JB/T NB/T等特殊标準材料

聯系人：江先生/龔小姐
手機： 15386611087, 17780160614
微信：15386611087, 17780160614

生產規格：電渣錠，電渣鋼；鋼棒，鍛件，闆等。

詢價

上海晟通金屬科技有限公司

主營: 特殊鋼不鏽鋼銅合金钛合金高溫合金耐蝕合金精密合金耐熱鋼鎳基焊絲模具鋼

聯系人：陳經理
手機： 18616886059
電話：021-33552688
微信：18616886059

棒材、線材、闆材、帶材、無縫管、法蘭、标準件、管件

詢價

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！

版權說明：
⑴ 本網站的所有内容（包括但不限于文字、圖片、音頻、視頻等）均受到版權保護，版權歸本網站所有；
⑵ 未經授權，禁止以任何形式轉載、複制、傳播或用于其他商業用途；
⑶ 如需使用本網站内容，請提前獲得授權。

材料與專利鋼号免責聲明：
⑴ 本平台所收錄的部分材料牌号為企業專利鋼号或專有命名牌号，非 GB、ISO、DIN、ASTM、JIS 等通用标準鋼号；
⑵ 相關化學成分、力學性能及适用範圍以專利文件、權利人公開資料或供方技術文件為準；
⑶ 平台所展示信息僅用于材料檢索、工程參考及技術對比，不構成等同、替代或采購依據。