AMS 5596 - SAE AMS 5596 M-2017-材數庫

牌号	AMS 5596
對應标準	SAE AMS 5596 M-2017 鎳合金，耐腐蝕和耐熱，薄闆，帶材，箔材和闆材 Nickel Alloy, Corrosion and Heat-Resistant, Sheet, Strip, Foil and Plate, 52.5Ni - 19Cr - 3.0Mo - 5.1 Cb (Nb) - 0.90Ti - 0.50AI - 18Fe, Consumable Electrode Remelted or Vacuum Induction Melted 1775 °F (968°C) Solution Heat Treated
歸類	合金鋼

AMS 5596 化學元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Ni	Cu	Mo	Ti	Nb	B	Co	Al	Ta	更多
最小值	-	-	-	-	-	17	50	-	2.8	0.65	4.75	-	-	0.2	-	Fe餘量
最大值	0.08	0.35	0.35	0.015	0.015	21	55	0.3	3.3	1.15	5.5	0.006	1	0.8	0.05	Fe餘量

AMS 5596 機械性能

厚度 t mm	熱處理或狀态	抗拉強度 σ_b Mpa	屈服點 σ_s Mpa	斷後伸長率或延伸率 δ %	硬度 HBW
t≤0.01	As Solution	≤965		report
0.01＜t≤0.1874	As Solution	≤965		≥30	HRB ≤102
0.1874＜t≤1.00	As Solution	≤1034		≥30	HRC ≥25
t≤0.25	After Precipitation/At Room Temperature	≥1241	≥1034	report
0.25＜t≤25.4	After Precipitation/At Room Temperature	≥1241	≥1034	≥12
t≤0.64	After Precipitation/At 649 °C	≥965	≥793	≥5
0.64＜t≤25.4	After Precipitation/At 649 °C	≥1000	≥827	≥5

注1：Elongation in 2 Inches or 4D.
注2：At Room Temperature：Determined in accordance with ASTM E8/E8M.
注3：At 1200 °F (649 °C)：Determined in accordance with ASTM E21 on specimens heated to 1200 °F 土5 °F (649 °C 士3 °C) , held at heat for not less than 20 minutes before testing, and tested at 1200 ° F 士5 °F (649 °C 士3 °C) .

材料牌号對應供應商

告訴我在“材數庫”看到，将給您優惠

上海亞螺精密緊固技術有限公司

主營: 各類不鏽鋼緊固件各類合金鋼緊固件特殊材質緊固件螺塞/堵頭耐高溫不鏽鋼緊固件 A4-80螺栓

聯系人：徐海
手機： 18621311857
電話：021-59766477

詢價

注：數據僅供參考！如有疑問，請填寫"我要糾錯"！

版權說明：
⑴ 本網站的所有内容（包括但不限于文字、圖片、音頻、視頻等）均受到版權保護，版權歸本網站所有；
⑵ 未經授權，禁止以任何形式轉載、複制、傳播或用于其他商業用途；
⑶ 如需使用本網站内容，請提前獲得授權。

材料與專利鋼号免責聲明：
⑴ 本平台所收錄的部分材料牌号為企業專利鋼号或專有命名牌号，非 GB、ISO、DIN、ASTM、JIS 等通用标準鋼号；
⑵ 相關化學成分、力學性能及适用範圍以專利文件、權利人公開資料或供方技術文件為準；
⑶ 平台所展示信息僅用于材料檢索、工程參考及技術對比，不構成等同、替代或采購依據。