牌号 X2CrNiN18-10
1.4311
對應标準 NF EN 10028-7-2000
壓力容器用不鏽鋼扁平產品
Flat products made of steels for pressure purposes Part 7: Stainless steels
歸類 奧氏體不鏽鋼
标簽 标準等級
X2CrNiN18-10 化學元素成分含量(%)
成分 C Si Mn P S Cr Ni N
最小值 - - - - - 17 8.5 0.12
最大值 0.03 1 2 0.045 0.015 19.5 11.5 0.22
◎ 未經買方同意，不得随意向鋼中添加表中未列的元素，冶煉精加工除外。采取一切必要措施以防在廢鋼和生產原料中帶入這些元素，因為其會削弱鋼的機械性能，降低鋼的适用性。
碳當量計算
X2CrNiN18-10 機械性能
條件 熱處理或狀态
抗拉強度
σb
Mpa 		屈服點
σs
Mpa 		斷後伸長率或延伸率
δ
% 		沖擊吸收能量
KV2
J
C：T ≤ 6 +AT 550~750 Rp0.2：≥290
Rp1.0：≥320
①②		 T ＜ 3mm: ≥40
T ≥ 3mm: ≥ 40
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
H：T ≤ 12 +AT 550~750 Rp0.2：≥270
Rp1.0：≥310
①②		 T ＜ 3mm: ≥40
T ≥ 3mm: ≥ 40
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
P：T ≤ 75 +AT 550~750 Rp0.2：≥270
Rp1.0：≥310
①②		 T ＜ 3mm: ≥40
T ≥ 3mm: ≥ 40
②③		 20℃：
(l: ≥100；t: ≥60)
-196℃：
(t: ≥60)
鋼材：20℃ ④ - ≥550 Rp0.2：≥270
Rp1.0：≥310
≥40 -
鋼材：-80℃ ④ - ≥850 Rp0.2：≥350
Rp1.0：≥420
≥40 -
鋼材：-150℃ ④ - ≥1050 Rp0.2：≥450
Rp1.0：≥550
≥35 -
鋼材：-196℃ ④ - ≥1250 Rp0.2：≥550
Rp1.0：≥650
≥35 -
◎C- 冷軋帶鋼; H- 熱軋帶鋼; P- 熱軋中厚闆；T- 厚度；t- 橫向；l-縱向。
◎+A=軟化退火；+AT=固溶退火；+QT=淬火及回火；+RA=再結晶退火。
◎ 如果熱加工和随後冷卻的條件符合ENISO3651-2中對產品機械性能和抗晶間腐蝕性的要求，則可以省略固溶處理。
*抗晶間腐蝕根據EN ISO 3651-2進行測試。在交貨條件下：有；在緻敏狀态下：有。
① 對于連續熱軋產品，可在詢價和訂購時商定Rp0.2(即表中σs)的最小值提高20MPa，Rp1.0的最小值提高10MPa。
② 如果在軋制寬度<300mm的帶材情況下，采用縱向試驗件，最小值減小如下:屈服強度-15MPa，恒定标距的延伸率-5%，比例标距延伸率-2%。
③ T＜3mm：該值适用于标距為80mm、寬度為20mm的試件，也可以使用标距為50mm、寬度為12.5mm的試件。T ≥3mm：該值适用于标距為5.65√S的試件。
④ 适用于20℃至-196℃之間的任何溫度，機械性能可通過線性插值估計。

  • 高溫下的最小屈服強度

    Material designationHeat treatment
    condition    		Minimum 0.2% proof strength Rp0.2,MPa
    at a temperature (in°C) of:
    Name Number100150200250300350400450500550600
    X2CrNiN18-101.4311+AT205175157145136130125121119118-
    Minimum 1.0% proof strength Rp1.0,MPa
    at a temperature (in°C) of:
    100150200250300350400450500550600
    240210187175167161156152149147-

  • 高溫下的最小抗拉強度

    Material designationMinimum tensile strength Rm,MPa
    at a temperature (in°C) of:
    Name Number100150200250300350400450500550600
    X2CrNiN18-101.4311490460430420410410-----

  • 熱處理指南

    Material designationHot formingHeat
    treatment
    symbol    		 Solution anneailing
    ①②    		Post weld heat 
    treatment
    Steel with ≤ 0.03% C
    Name NumberTemperature
    ℃    		Type of
    cooling    		Temperature
    ℃ ③④    		Type of
    cooling    		Temperature
    ℃ ⑥    		Type of
    cooling
    X2CrNiN18-101.43111150 to 850air+AT1000 to 1100water,air ⑤900 to 940air 
    ◎ a=air; o=oil; w=water.
    ◎ Scale and annealing colours produced during hot forming, heat treatment or welding may adversely affect the corrosion resistance. They should be removed as far as possible before use, e.g. by pickling.
    ◎ The temperatures of annealing should be agreed for simulated heat treated test pieces.
    ① The solution treatment may be omitted if the conditions for hot working and subsequent cooling are such that the requirements for the mechanical properties of the product and the resistance to intergranular corrosion as defined in EN ISO 3651-2 are obtained and provided these requirements are met even after appropriate subsequent solution annealing.
    ② Re-crystallizing annealing.
    ③ If heat treatment is carried out in a continuous furnace, the upper part of the range specified is usually preferred, or even exceeded.
    ④ The lower end of the range specified for solution annealing should be aimed at for heat treatment as part of further processing,because otherwise the mechanical properties might be affected. If the temperature of hot forming does not drop below the lower temperature for solution annealing.a temperature of 980℃ is adequate as a lower limit for Mo-free steels,a temperature of 1000℃ for steels with Mo contents up to 3% and a temperature of 1020℃ for steets with Mo contents exceeding 3%.
    ⑤ cooling sufficiently rapid.
    ⑥ Minimum holding time:30min.

X2CrNiN18-10 對應不同标準
1 EN 10088-1-2005 不鏽鋼 第1部分:不鏽鋼的清單
X2CrNiN 18-10 1.4311
2 EN 10296-2-2005 機械工程和一般工程用焊接圓鋼管.交貨技術條件.第2部分:不鏽鋼
X2CrNiN18-10 1.4311
3 EN 10253-4-2003 對接焊管道接頭.具有特殊檢驗要求的鍛制奧氏體和鐵素體－奧氏體(二相)不鏽鋼
X2CrNiN18-10 1.4311
4 EN 10250-4-1999 一般工程用途的自由鍛鋼鍛件:不鏽鋼
X2CrNiN 18-10 1.4311
5 DIN 17440-1972 不鏽鋼質量标準
X2CrNiN 18-10 1.4311
6 EN 10088-3-2005 不鏽鋼第3部分：一般用途的半成品，鋼棒，軋制線材和型鋼的交貨條件
X2CrNiN18-10 1.4311
7 ISO 9327(-5)-1999 承壓鋼鍛件和軋制或鍛制不鏽鋼棒-技術交付條件-第5部分：不鏽鋼
X2CrNiN18-10
8 EN 10269-2013 規定高溫和/或低溫性能的緊固件用鋼和鎳合金
X2CrNiN 18-10 1.4311
9 EN 10088-3-2014 不鏽鋼 - 第3部分：半成品，棒材，杆材，線材，型材和光亮產品的一般用途耐腐蝕鋼的交貨技術條件
X2CrNiN18-10 1.4311
10 DIN EN 10269-2014 規定高溫和/或低溫性能的緊固件用鋼和鎳合金
X2CrNiN 18-10 1.4311
11 ISO 9328-7-2018 不鏽鋼承壓扁鋼制品
X2CrNiN18-10
12 DIN EN 10088-3-2014 不鏽鋼-半成品、棒材、杆材、線材、型材及光亮產品交貨技術條件
X2CrNiN18-10 1.4311
13 NF EN 10088-2-2005 普通用途不鏽鋼闆和鋼帶的交貨技術條件
X2CrNiN18-10 1.4311
14 NF EN 10088-1-2005 不鏽鋼 - 第1部分：不鏽鋼清單
X2CrNiN18-10 1.4311
15 NF EN 10028-7-2008 壓力容器用不鏽鋼扁平產品
X2CrNiN18-10 1.4311
16 NF EN 10296-2-2005 機械和一般工程用焊接圓鋼管-交貨技術條件-第2部分:不鏽鋼管
X2CrNiN18-10 1.4311
17 NF EN 10028-7-2000 壓力容器用不鏽鋼扁平產品
X2CrNiN18-10 1.4311